Development of Perforating Die for Manufacturing Fine Multi-perforated type Nail Files

미세 다수공 타입의 네일파일 제조용 퍼퍼레이팅 금형 개발

0.5mm thick steel is used to manufacture nail files. The first process is blanking and the second process is making about 300 holes of 0.8-l.0mm in diameter. This process depends mainly on etching which takes 33% of manufacturing cost and it can make manufacturing cost rise. The residual etching reagent is not environmentally friendly and the steel material is apt to rust as well. To solve these problems, researches on the following subjects are performed: proper material to prevent from rusting and strip layout strategies in stamping to replace etching process with press process which makes use of die. And new quill type punch is developed to replace the regular standard punch, one of the die parts, which frequently get broken while working. And these researches and developments lead to develop a progressive perforating die.

네일 파일(nail file)을 제조할 때 재료는 강판(두께 0.5㎜)을 사용하고 가공방법은 외형형상을 만들고 Φ 0.8-Φ 1.0㎜의 구멍을 약 300여개 뚫어 완성한다. 이들의 가공방법은 에칭(etching)에 의존하여 제조원가의 33%를 에칭비가 차지하고 있으므로 제조원가의 상승원인이 되고 에칭시 부식제(etching reagent)의 잔류도 환경 친화적이 못되며 재료가 강판이기 때문에 제품에 녹(rust)이 생기므로 이들의 문제점을 해결하고자 다음과 같이 연구개발을 수행하였다. 제품의 녹 방지를 할수 있는 적합한 재질 선택 방법을 고찰하고, 에칭 가공방법을 사용하지 않고 금형을 이용한 프레스 가공으로 교체하기 위하여 프레스 스탬핑시의 스트립 레이아웃(strip layout)기법을 연구개발하고, 금형 부품 중에서 작업 중 절손이 빈번한 보통의 표준펀치를 퀼형의 펀치로 개발 하므로써 프로그레시브 퍼퍼레이팅 금형(progressive perforating die)을 개발하게 되었다.