A Study on Fatigue Fracture Behaviour of Surface Crack in Finite Plates and Fillet Weldment

유한평판 및 필렛 용접부에 있어서 표면균열의 피로 파괴거동에 관한 연구

  • 한문식 (계명대학교 기계ㆍ자동차공학부)
  • Published : 2004.07.01
Download PDF
⟨ Previous Next ⟩

Abstract

Fatigue crack growth from surface defects is one of the most important subjects for the evaluation and the assurance of safety in pressure vessels, piping systems, LPG/LNG fuel tank and other various structures. This paper attempts to analysis some practical or general problems such as the estimation of crack growth life to penetrate the plate thickness, based on fatigue crack growth a single surface flaw and the interaction of multiple flaws. An experiment on the coalescence of multiple undercuts was carried out under cyclic tension condition as a attempt to the analysis of multiple crack problems. It is noted that the fracture strength is characterized by the analogy to that in a single crack growth.

Keywords

References

  1. Engng Fract. Mech. v.20 Multiple Surface Cracks in Pressure Vessels P.E.O'Donoghue;T.Nishioka;S.N.Atluri https://doi.org/10.1016/0013-7944(84)90059-6
  2. Int. J. of Fatigue v.26 no.1 Fatigue Life Duration Prediction for Welded Spots by Volumetric Method H.Adib;J.Gilgert;G.Pluvinage
  3. Transactions of KSAE v.11 no.1 Fatigue Characteristics of SPFC590 Laser Welded Sheet Metal for Automobile Body Panel M.S.Han;Y.S.Lee
  4. J. of JSME v.87 Fatigue of Worked Metallic Member and Structure S.Ohta
  5. Journal of SNAJ v.147 Empirical Expressions of Surface Fatigue Crack Shape K.lida;Y.Kho
  6. Engineering Fracture Mechanics v.3 A Study of Techniques for Obtaining Partial Thickness Cracks of PreSelected Depths and Shapes D.L.Corn https://doi.org/10.1016/0013-7944(71)90050-6
  7. Fatigue Fract. Engng Mater. Struct v.14 no.1 The Propagation on Non-coplanar Semi-elliptical Fatigue Cracks W.O.Soboyejo;J.F.Knott https://doi.org/10.1111/j.1460-2695.1991.tb00641.x
  8. Proc. Instn Mech. Engrs 202 no.C1 Aspect of Fatigue Crack Growth M.W.Brown
  9. Journal of Applied Mechanical Transaction of ASME, E v.84 Crack-extension Force for a Part-through Crack in a Plate G.R.Irwin
  10. Int. J. of Fatigue v.4 no.4 A Critical Review of Crack Tip Stress Intensity Factors for Semi-elliptical Cracks P.M.Scott;T.W.Thorpe
  11. Engineering Fracture Mechanics v.15 no.1-2 An Empirical Stress Intensity Factor Equation for the Surface Crack J.E.Newman,Jr.;I.S.Raju https://doi.org/10.1016/0013-7944(81)90116-8
  12. Int. J. of Fracture v.40 Stress Intensity Factors for Semi-elliptical Surface Cracks in Welded Joints X.Niu;G.Glinka https://doi.org/10.1007/BF00963660
  13. ASTM Specification E647-86A Standard Test Method for Measurements of Fatigue Crack Growth Rates
  14. 1984 Annual Book of ASTM Standards 03.10. (1) Standard Test Method for Constant-Load-Amplitude Fatigue Crack Growth Rates Above 10-8m/cycle
  15. Fatigue Engng Mater. Struct. v.12 no.3 A Study of the Interaction and Coalescence of Two Coplanar Fatigue Cracks in Bending W.O.Soboyejo;R.A.Smith;J.F.Knott https://doi.org/10.1111/j.1460-2695.1989.tb00524.x
  16. Int. Cong. on Fatigue of Welded Constructions, Paper No. 35 Interaction of Multiple Fatigue Cracks H.G.Morgan
  17. BOSS '88 Fatigue Crack Growth Modeling for Multiple Initiated Cracks at Weld Toesin Tubular Joints H.H.Snijder