Magnetic Properties of Ni Nanostructures Made by using Nanoporous Anodic Alumina

AAO를 이용한 Ni 나노구조체의 자기적 특징

  • Published : 2004.06.01
Download PDF
⟨ Previous Next ⟩

Abstract

Array of magnetic Ni nanostructures has been fabricated on Si substrate by using nanoporous alumina film as a mask during deposition. The nanostructures are truncated cone-shape and the lateral sizes are comparable to height. While the continuous film shows well-defined in-plane magnetization, the nanostructure shows perpendicular component of magnetization at remanence. The hysterectic behavior of nanostructures is dominated by the demagnetizing field instead of interaction among them.

나노크기의 기공을 갖는 AAO(Anodic Aluminum Oxide)를 이용하여 Si 기판 위에 열 증착 방식으로 Ni 나노구조체를 제작하였다. 제작된 나노구조체는 직경과 높이가 80nm정도로 거의 비슷한 원기둥 형태를 보였다. Ni 나노구조체의 자기적 특성은 광자기효과(Magneto-Optic Kerr effect)를 이용하여 측정하였고, 함께 성장시킨 박막(continuous film)과 비교하였다. 종횡비(aspect ratio)가 1 : 1 정도인 나노구조체의 자화용이축은 평면방향으로 자화용이축을 보이는 박막과는 달리 수직자기이방성을 보여주었으며, 수직 및 수평방향으로 자기장을 가하면서 얻은 자기이력곡선(hysteresis loop)으로부터 나노구조체의 포화자기장(saturation field)과 보자력(coercivity)이 박막과는 많은 차이를 보였다. 박막에서 거의 무시할 만한 값을 갖는 수직방향의 자기이력곡선에서 측정된 잔류자화(remanent magnetization) 나노구조체에서는 0.3으로 크게 증가했다.

Keywords

References

  1. IEEE Trans. Magn. v.35 D.Weller;A.Moser https://doi.org/10.1109/20.809134
  2. Science v.254 G.M.Whitesides;J.P.Mathias;C.T.Seto https://doi.org/10.1126/science.1962191
  3. Science v.276 M.Park;C.Harrison;P.M.Chaikin;R.A.Register;D.H.Adamson https://doi.org/10.1126/science.276.5317.1401
  4. Science v.268 H.Masuda;K.Fukuda https://doi.org/10.1126/science.268.5216.1466
  5. Appl. Phys. Lett. v.71 H.Masuda;H.Yamada;M.Satoh;H.Asoh;M.Nakao;T.Tamamura https://doi.org/10.1063/1.120128
  6. Chaos v.12 S.K.Thamida;H.C.Chang https://doi.org/10.1063/1.1436499
  7. Appl. Phys. Lett. v.75 J.S.Suh;J.S.Lee https://doi.org/10.1063/1.124911
  8. J. Appl. Phys. v.85 J.M.Garcia;A.Asenjo;J.Velazquez;D.Garcia;M.Vazquez;P.Aranda;E.Ruiz-Hitzky https://doi.org/10.1063/1.369868
  9. Appl. Phys. Lett. v.78 H.Cao;C.Tie;Z.Xu;J.Hong;H.Sang https://doi.org/10.1063/1.1354156
  10. Appl. Phys. Lett. v.79 K.Nielsch;R.B.Wehrspohn;J.Barthel;J.Kirschner;U.Gosele https://doi.org/10.1063/1.1399006
  11. Appl. Phys. Lett. v.79 A.J.Yin;J.Li;W.Jian;A.J.Bennett;J.M.Xu https://doi.org/10.1063/1.1389765
  12. J. Appl. Phys. v.91 J.Liang;H.Chik;A.Yin;J.Xu https://doi.org/10.1063/1.1433173
  13. Appl. Phys. Lett. v.76 D.Crouse;Y.H.Lo;A.E.Miller;M.Crouse https://doi.org/10.1063/1.125652
  14. Jpn. J. Appl. Phys. v.40 H.Masuda;K.Yasui;Y.Sakamoto;M.Nakao;T.Tamamura;K.Nishio https://doi.org/10.1143/JJAP.40.L1267
  15. Appl. Phys. Lett. v.82 P.L.Chen;C.T.Kuo;T.G.Tsai;B.W.Wu;C.C.Hsu;F.M.Pan https://doi.org/10.1063/1.1571661
  16. Appl. Phys. Lett. v.81 Z.Sun;H.K.Kim https://doi.org/10.1063/1.1517719
  17. Modern Magnetic Materials Principle and Applications R.C.O'Handley
  18. Introduction to magnetic materials B.D.Cullity