INFLUENCE OF TIP DISTANCE ON DEGREE OF CONVERSION OF COMPOSITE RESIN IN CURING WITH VARIOUS LIGHT SOURCES

광원에 따른 조사거리의 증가가 복합레진의 중합도에 미치는 영향

Recently, newly developed single high-intensity LED curing lights for composite resins are claimed to have a higher intensity than previous LED curing lights and to results in optimal properties and short curing time. The purpose of this study was to determine the curing effectiveness of the curing units and to evaluate the relationship between the degree of polymerization and distance from curing light tip end to resin surface. One composite resin was tested(Filtek Z250). Thin film specimens were cured with a LED curing unit(Elipar Freelight 2, 10s), Plasma Arc curing unit(Flipo, 6s), Halogen curing light(XL3000, 20s) at four curing light tip to the resin surface(0mm, 2mm, 4mm, 6mm). Degree of conversion of composite resins were determined by a Fourier Transform Infrared Spectrometer(FTIR). From the present study, the following results were obtained. 1. In all curing units, relative light intensity was significantly decreased according to the increase of distance of light tip to the resin surface(p<0.05). LED curing units showed a higher percentile decrease in intensity than other curing units. 2. In all curing units, degree of conversion was decreased as increase of the distance but no statistically significant difference(p>0.05) except between 4mm and 6mm(p<0.05). 3. When comparing degree of conversion of light curing units at each distance(0mm, 2mm, 4mm, 6mm), LED curing light had a higher degree of conversion than plasma arc and halogen curing lights at 0, 2, 4mm(p<0.05). At 6mm, there was a no significant difference among the curing units(p>0.05).

최근에 소개된 single high-intensity LED 중합기는 이전의 LED 중합기에 비해 높은 광도를 가지며 짧은 중합시간에 적절한 물성을 가질 수 있다고 한다. 본 연구는 single high-intensity LED 중합기의 중합성능을 평가하기 위하여 거리에 따른 중합도를 조사하였다. Mylar strip사이에 복합레진(Filtek Z250)을 넣고 압접시켜 만든 얇은 필름형 시편을 LED 중합기(Elipar Freelight 2, 10초), 플라스마 중합기(Flipo, 6초)와 할로겐 중합기 (XL3000, 20초)를 사용해 0mm, 2mm, 4mm, 6mm에서 광도를 측정하고 중합시켰다. 중합된 시편을 Fourier Transform Infrared Spectrometer(FTIR)를 이용해 중합도를 측정한 후 다음과 같은 결론을 얻었다. 1. 모든 중합기에서 거리가 증가할수록 유의하게 광도가 감소하였으며 LED중합기의 경우 6mm에서 다른 중합기에 비해 가장 많은 광도 감소율을 보였다(p<0.05). 2. 모든 중합기에서 거리가 증가함에 따라 4mm까지는 중합도가 감소하였지만 유의한 차이는 보이지 않았다(p>0.05). 하지만 4mm와 6mm사이에서는 모든 중합기에서 유의하게 감소하였다(p<0.05). 3. 각 거리에 따른 중합기간의 중합도 차이는 0mm, 2mm, 4 mm에서 LED중합기가 다른 중합기보다 유의하게 높은 중합도를 보였으며 (p<0.05) 플라스마 중합기와 할로겐 중합기 사이에서는 유의한 차이가 없었다. 하지만 6 mm에서는 모든 중합기 사이에 유의한 차이를 보이지 않았다(p>0.05).