Change of Surface Temperature in Woodceramics Made from MDF(II) - Effect of Impregnation Rate and Burning Temperature -
MDF로 제조된 우드세라믹의 표면온도 변화(II) - 수지 함침율과 소성온도의 영향 -
- Oh, Seung Won (College of Agriculture, Chonbuk National University) ;
- Byeon, Hee Seop (College of Agriculture and the Institute of Agriculture and Life Science, Gyeongsang National University)
- Received : 2002.06.20
- Accepted : 2002.07.10
- Published : 2003.02.26
Abstract
In this study, woodceramics were made from MDF with various resin impregnation rate. To investigate the change of surface temperature of woodceramics, the impregnated MDF was burned at the temp. 600, 800, 1,000, 1,200℃. Surface temperature of woodceramics was increased as impregnation rate and burning temperature was increased. The specimen burned at 800℃ was lower than others. Change of temperature under given temperature increased as time passed and it showed more increased in temperature at burning temperature of 1,200℃. Change of surface temperature increased when floor temperature increased and the temperature was 49.2℃ at 70℃ in floor temperature of 1,200℃ specimen. The decent in surface temperature of woodceramics was the fastest decrease at the burning temperature of 800℃ specimen.
MDF를 재료로 600, 800, 1,000, 1,200℃에서 소성 하여 우드세라믹을 제조한 후 소성 전 수지 함침율과 소성온도에 따른 우드세라믹의 표면온도를 조사하였다. 함침율, 소성온도 및 시간의 경과에 따라 표면온도가 증가하였으며, 1,200℃ 시료의 온도가 가장 높게 나타났다. 시간의 경과에 따른 표면온도의 하강은 800℃ 시료의 온도가 가장 빨리 감소하였다.