Physical Properties of Liquid Ammonia Wood for Bending

휨가공을 위한 액체암모니아 처리재의 물리적 성질

The physical properties of small hardwood and softwood specimens treated with liquid ammonia were investigated. The specimens treated for 4 or 18 hours were compared with the controls. The EMCs of the liquid ammonia treated specimens were higher than those of the controls when conditioned at the same humidities. However once oven-dried they didn't show any significant differences in EMCs. With the increase of liquid ammonia treatment time specimens shrank in radial and tangential directions, but not in longitudinal direction. As liquid ammonia treatment time increased the ultrasonic velocities of specimens decreased and their densities increased, thus their dynamic MOEs decreased. For chestnut specimens the presteamed were more plasticized than the liquid ammonia treated. Incising on the surfaces of specimens didn't improve liquid ammonia permeability in both hardwoods and softwoods. Liquid ammonia treatment was very effective for plasticizing 5 mm thick softwoods. Relative dielectric constants and thermal conductivities were measured with both liquid ammonia treated and control specimens.

액체암모니아 처리 침·활엽수 소시편의 물리적 성질을 무처리와 비교하였다. 처리시간은 4와 8시간으로 하였다. 동일한 환경에서 처리재의 평형함수율은 무처리재보다 항상 높았으나 전건 후에는 차이를 나타내지 않았다. 암모니아 처리를 오래할수록 방사방향과 접선방향으로 수축이 일어났으나 섬유방향에는 변화가 없었다. 또 처리시간이 길수록 초음파 전달속도는 감소하고 밀도는 증가하였다. 따라서 동탄성계수는 감소함을 보였다. 밤나무의 가소화는 증기처리가 액체 암모니아 처리보다 효과 있음과 인사이징이 침·활엽수 모두 액체 암모니아 침투성을 높이지 못했음이 밝혀졌다. 액체 암모니아 처리는 5mm두께 침엽수 시편에서 제일 좋은 가소화 효과를 보였다. 상대유전율과 열전달계수도 측정하여 처리재와 무처리재를 비교하였다.