Weathering of Prunus sargentii Specimens Modified with Acetic Anhydride and Formaldehyde Vapor

무수초산 및 포름알데하이드 기상처리 산벚나무의 야외폭로 및 촉진열화

Small cherry specimens modified with acetic anhydride and formaldehyde vapor phase were weathered by outdoor exposure and accelerated conditioning in a climate chamber. The effects of the chemical modification were evaluated by measuring their weight percentage gains (WPG), hygroscopicity and color differences before and after weathering. The average WPGs of the 72 hour acetylated and formaldehyde-treated specimens were 8.1 and 15.7%, respectively. After outdoor exposure for more than 2 months, the acetylated specimens lost weights by only 1.5%, but the formaldehyde-treated did much more than the formers. It was revealed that acetylation reduced the hygroscopicity and discoloration of wood while formaldehyde treatment didn't. Moreover the longer is the formaldehyde treatment time the more degraded after weathering. It was concluded that the vapor-phase acetylation could be applied for improving the dimensional stability of old wooden blocks.

고목재의 치수안정성을 향상시키는 무수초산과 포름알데하이드 기상처리가 팔만대장경 경판의 주요 소재인 산벚나무의 중량, 흡습성, 그리고 재색에 미치는 효과를 야외폭로와 촉진열화시험을 통해 측정하였다. 무수초산과 포름알데하이드 72시간 기상처리에 의한 시편의 중량은 각각 평균 8.1과 15.7% 증가하였다. 두 달 이상 야외 폭로된 아세틸화 시편의 중량은 1.5% 밖에 감소하지 않았으나 포름알데하이드 시편은 매우 많이 감소하였다. 또 아세틸화 처리는 시편의 흡습성을 낮추었으며 자외선에 의한 갈변을 방지하였으나, 포름알데하이드 처리는 그렇지 못하였다. 한편 포름알데하이드 처리시간이 긴 시편일수록 할열과 변형이 더 많이 발생하였다. 따라서 포름알데하이드 처리는 고목재 보존방법으로 맞지 않으나, 아세틸화 기상처리는 액상처리와 같이 중량을 과도하게 증가시키지 않으면서도 자외선과 비로 인한 재색변화와 중량감소를 막아줌으로 고목재의 보존처리에 적합하다고 할 수 있다.