Study of Aging and Durability on Plasma Polymerized Tire Cords
플라즈마 중합 코팅된 타이어 코드의 노화에 따른 접착력 변화 연구
- Kang, H.M. (Department of Materials Science and Engineering, Kwangju Institute of Science and Technology) ;
- Yoon, T.H. (Department of Materials Science and Engineering, Kwangju Institute of Science and Technology)
- Received : 2003.02.06
- Accepted : 2003.03.08
- Published : 2003.03.25
Abstract
Steel tire cords were subjected to plasma polymerization coating of acetylene in order to enhance the adhesion to rubber compounds. Plasma polymerization coating was varied to plasma polymerization coating of acetylene, argon plasma etching+plasma polymerization, or argon plasma. etching+plasma polymerization with Ar carrier gas. Adhesion was evaluated via TCAT samples and compared to those with brass coated tire cord. For durability study, plasma polymer cooled tire cords were aged in lab atmosphere for 1, 3, 5, 10 or 15 days, while TCAT specimens prepared with plasma polymer coated tire cords were aged in distilled water, 10% NaCl solution or
강철 타이어 코드의 접착력 향상을 위하여 아세틸렌 플라즈마 중합 코팅, 아르곤 에칭+아세틸렌 플라즈마 중합 코팅, 그리고 아르곤 에칭+담채를 이용한 아세틸렌 플라즈마 중합 코팅을 실시하였으며, 접착력은 TCAT시편으로 측정하였다. 플라즈마 중합 코팅된 타이어 코드의 내구성을 고찰하기 위하여 제 1 단계로 아세틸렌 플라즈마 중합 코팅된 타이어코드를 상온에서 1, 3, 5, 10, 15일 동안 방치한 후 TCAT 시편을 제조하여 접착력변화를 측정하였으며, 제 2 단계로는 플라즈마 중합 코팅된 코드로 TCAT 시편을 제조한 후 증류수, 10% NaCl 수용액에서 또는