Abstract
To use ferro copper slag as aggregate in the construction, an evaluation upon the two kinds of ferro copper slag being produced was conducted to determine the basic physical, and mechanical properties, chemical component and environmental noxiousness. As a result of experiment, it was found that two kinds of ferro copper slag satisfies the physical and mechanical properties of aggregate, prescribed in KS F 2526, and that in the result of noxious heavy metal eruption test by single bach extraction, no eruption of noxious heavy metal was detected or the eruption was far below the reference value. And mortar test was conducted by replacing sand of 25, 50, 75, 100% and the performance level was presented upon reviewing the fluidity property and variable aspects of unit weight. The increase of strength in accordance with replacement rate of sand was found to be the below than the equivalent level compared to the testing specimens that did not use ferro copper slag, but those of 25% replacement rate was above than 0%. Thus, two kinds of ferro copper slag, produced in the domestic, were found to be possessing the enough physical properties to use as concrete aggregate assuming that used with sand and in particular, it was reviewed to be advantageous in manufacturing concrete or mortar that requires weight.
동슬래그를 콘크리트용 골재로 활용하기 위하여 국내에서 생산되고 있는 2종의 동슬래그에 대해 골재의 기초적인 물리 역학적 특성과, 화학성분, 환경 유해성 평가를 실시하였다. 실험결과, 2종의 동슬래그는 KS F 2526에서 규정하고 있는 골재의 물리.역학적 특성을 만족하고 있으며, 폐기물공정시험법에 의한 유해 중금속 용출시험 결과, 유해 중금속의 용출이 전혀 없거나 기준치를 크게 하회하는 것으로 나타났다. 또한, 천연모래를 25, 50, 75, 100%를 치환하여 모르타르 실험을 실시하고, 슬래그의 치환비율에 따른 유동특성 및 단위용적중량의 변동양상을 검토하여 그 성능수준을 제시하였다. 슬래그의 치환비율에 따른 강도의 증가는 동슬래그를 사용하지 않은 실험체와 비교하였을 경우, 동슬래그의 치환비율이 증가함에 따라 전체적으로 감소하는 경향이나, 25% 수준까지는 동등 이상의 수준이었다. 따라서 국내에서 생산되고 있는 2종의 자용로 및 연속로 슬래그는 천연모래와의 혼합사용을 전제로, 콘크리트용 골재로 사용하기에 충분한 물성을 지니는 것으로 나타났으며, 특히 중량이 요구되는 콘크리트 및 모르타르의 제작에 유리한 것으로 검토되었다.