Abstract
The estimation functions were proposed for calculating diffusion coefficient, chloride binding, and evaporable water. The program estimating chloride ion penetration was developed on the basis of these functions and the effects of humidity, curing temperature, water-cement ratio, and $C_3$A on chloride penetration were analyzed. The relative humidity increases the depth of chloride ion penetration and the trend becomes greater with aging. On the contrary, the influence of curing temperature on chloride ion penetration decreases with aging. By the way, the rise of $C_3$A in cement increases total chloride concentration on the surface as the bound chloride concentration increases but it decreases total chloride concentration on the inner part as the diffusion velocity of free chloride decreases. The fall of water-cement ratio decreases the chloride penetration depth rapidly. Therefore, the reduction of water-cement ratio may be the most effective method for reducing of the steel corrosion by chloride penetration.
본 논문에서는 염소이온 침투해석에 사용되는 염소이온 확산계수. 염소이온 고정화 관계식, 증발가능 수량에 대한 일반 예측식들을 제시하였다. 이러한 식들을 염소이온 확산 모델링에 대입하여 그 식들의 유효성을 검토하였다. 상대습도와 양생온도의 염소이온 확산에 대한 영향은 주로 확산계수를 변화시켜 고려한다. 상대습도가 증가하면 염소이온 확산깊이는 증가하고 재령이 경과할수록 상대습도가 확산깊이에 미치는 영향은 커진다. 반면에, 양생온도가 증가하면 확산깊이가 조금 증가하지만 재령이 경과할수록 양생온도가 확산깊이에 미치는 영향은 감소한다. 한편, 염소이온의 고정화에 영향을 미치는 시멘트의 $C_3$A양이 증가하면 표면에서는 고정염소이온의 증가로 인해 전체 염소이온량이 증가하지만 깊이가 깊어질수록 확산되는 자유염소이온의 감소로 인해 전체 염소이온량이 감소한다. 물-시멘트비가 감소하면 염소이온의 확산깊이는 급격히 감소하고 염소이온의 확산을 막는 가장 효과적인 방법은 물-시멘트비를 감소시키는 것임을 알 수 있다