Dielectric and Magnetic Properties of Co-doped Ni0.65Zn0.35Fe2O4 Thin Films Prepared by Using a Sol-gel Method

  • Lee, Hyun-Sook (Department of Computer and Electronic Physics, Sangji University) ;
  • Lee, Jae-Gwang (Department of Applied Physics. Konkuk University) ;
  • Baek, K.S. (Department of Physics, Yonsei University) ;
  • Oak, H.N. (Department of Physics, Yonsei University)
  • 발행 : 2003.12.01

초록

$Ni_{0.65}Zn_{0.35}Fe_2O_4$thin films were prepared by using a sol-gel method. Their crystallographic, dielectric and magnetic properties were investigated as a function of Cu contents by means of an X-ray diffractometer (XRD), X-ray reflectivity, LCZ meter (NF2232), a vibrating sample magnetometer (VSM), and an atomic force microscope (AFM). From typical C-V measurements for $Ni_{0.65}Zn_{0.35}Fe_2O_4$ thin films on p-type silicon substrate, the surface charge density was calculated as 1.4 ${\mu}$C/$m^2$. The dielectric constant evaluated from the capacitance at the accumulation state was 28. The high $H_{c}$ and low $M_{sat}$ at x=0.0 and 0.1 were due to the growth of the ${\alpha}$-$Fe_2O_3$ phase having antiferromagnetic properties. The rapidly decreased $H_{c}$ and increased $M_{sat}$ at x=0.2 and 0.3 can be explained that the ${\alpha}$-$Fe_2O_3$ phases have completely disappeared at x=0.3 and so, non-magnetic defects are minimized. The $M_{sat}$ was slightly decreased and the $H_{c}$ was increased above at x=0.3 because the increase of grain boundary due to smaller grain size acts as defects during magnetization process.

키워드

참고문헌

  1. Ceramic Bull v.66 K.Ishino;Y.Narumiya
  2. J. Kor. Mag. Soc. v.5 J.H.Nam;H.H.Jung;J.Y.Shin;J.H.Oh
  3. J. Phys. Ⅲ v.6 A.Dias;N.D.S.Mohallem;R.L.Moreira
  4. J. Appl. Phys. v.81 P.S.Aril Kumar;J.J.Shrotri;C.E.deshpande;S.K.Date https://doi.org/10.1063/1.365464
  5. J. Appl. Phys. v.61 G.Dionne;R.West https://doi.org/10.1063/1.338623
  6. J. Magn. Magn. Mater v.131 S.A.Olofa https://doi.org/10.1016/0304-8853(94)90016-7
  7. J. Appl. Phys. v.73 P.C.Joshi;S.B.Krupanidhi https://doi.org/10.1063/1.353960
  8. Jpn. J. Appl. Phys. v.36 M.B.Lee;T.Ohnishi;T.Maeda;M.Kawasaki;M.Yoshimoto;H.Koinuma https://doi.org/10.1143/JJAP.36.6500