초록
Microstructure and shear strength of Sn-Zn lead-free solders and Au/Ni/Cu UBM joint under thermal aging conditions was investigated. The samples were aged isothermally at 10$0^{\circ}C$ and 15$0^{\circ}C$ for 300, 600, and 900 hours. The IMCs(Intermetallic Compound) at the interface between solder and UBM were examined by FESEM and TEM. The results showed that the shear strength was decreased with aging time and temperature. The solder ball with high activated RA flux had about 8.2% higher shear strength than that of RMA flux. Poor wetting and many voids were observed in the fractured solder joint with of RMA flux. The decreased shear strengths were caused by IMC growth and Zn grain coarsening. Zn reacted with Au and then was transformed to the $\beta$ -AuZn compound. Although AuZn grew first, $r-Ni_5Zn_{21}$ compounds were formed with aging time. The layers indicated by $Ni_5Zn_{21}(1)$, (2), and (3) were formed with the thickness of ∼0.7 ${\mu}{\textrm}{m}$, ∼4 ${\mu}{\textrm}{m}$, and ∼2 ${\mu}{\textrm}{m}$, respectively.