초록
We fabricated cube textured Ni substrate for YBCO coated conductor and evaluated the effects of processing parameters on microstructural evolution and texture formation. Ni-rods as an initial specimen were prepared by two different methods, i.e., powder metallurgy(PM) and plasma arc melting(PAM). Subsequently, the rods were cold rolled to 100 $\mu\textrm{m}$ thick substrate and annealed at temperatures of $700∼1200^{\circ}C$. The texture of the substrate was characterized by pole-figure. It was observed that the texture of substrate made by P/M did not significantly varied with annealing temperature of 600∼$l100^{\circ}C$ and the full-width at half-maximums (FWHM) of both in-plane and out-of-plane were 9$^{\circ}$∼$10^{\circ}$. On the other hand, the texture of substrate made by PAM was more dependent on the annealing temperature and the corresponding values were $9^{\circ}$ ∼$13^{\circ}$ at the temperature range. In addition, recrystallization twin texture, (221)<221>, was formed as the temperature increased further. OM profiles showed that the grain size of substrate made by P/M was smaller than that made by PAM and this difference was correlated to the microstructure of initial specimens.