A STUDY ON THE FORMATION OF SHEAR BONDING STRENGTH AND HYBRID LAYER ACCORDING TO THE APPLICATION TIME AND FREQUENCY OF AN ALL-IN-ONE SYSTEM IN PRIMARY TEETH.

유치에서 All-In-One system의 적용 시간과 적용 횟수에 따른 전단 결합 강도 및 혼성층 형성에 관한 연구

The purpose of the present study was to evaluate the patterns of hybrid layer according to the application time and the frequency and its effects on the shear bonding strength of All-In-One system in primary teeth. A single bonding agent(Scotchbond Multi-Purpose Plus, 3M) and an All-In-One system(Prompt L-pop, 3M ESPE) were applied on the dentin varying the application time and the frequency in primary teeth. Shear bond strength was measured and the patterns of hybrid layers were observed by SEM. The following results were obtained ; 1. The shear bonding strength of single bonding agent was significantly higher than that of All-In-One system(P<0.05). 2. The shear bonding strength of All-In-One system applied twice or 3 times were higher than that of applied once (P<0.05). And thickness of the hybrid layer was increased when applied twice or 3 times compared to once. 3. The shear bonding strength of All-In-One system when applied for 15 second and 30 second were higher than that of 7 second (P<0.05). And the hybrid layer thickness of 15 second and 30 second's application time were higher than that of 7 second. 4. Thickness of hybrid layer applied with single bonding agent was $2-4{\mu}m$ and that of All-In-One system was $1-2{\mu}m$.

본 연구는 All-In-One system의 적용 시간과 도포횟수에 따라 유치 상아질과 복합레진의 접착 강도와 혼성층에 어떤 영향을 미치는지를 규명하고자 Single bonding agent(Scotchbond Multi-Purpose Plus, 3M, USA)와 All-In-One system(Prompt-L pop, 3M ESPE, USA)를 사용하였고 수복용 레진으로 복합레진(Z-250, 3M, USA)를 사용한 결과 다음과 같은 결과를 얻을 수 있었다. 1. 전단 결합 강도는 Single bonding agent를 적용한 경우 All-In-One system을 적용한 군보다 유의하게 높게 나타났다(P<0.05). 2. Prompt L-pop을 2회, 3회 적용한 경우에 전단 결합 강도는 1회 적용한 군보다 유의하게 높게 나타났으며(P<0.05), 혼성층의 두께는 1회 적용군보다 2회, 3회 적용한 군에서 증가하였다. 3. Prompt L-pop을 15초 적용한 경우에 전단 결합 강도는 7초 적용한 군보다 유의하게 높게 나타났으며(P<0.05), 30초 적용군과는 차이가 없었다. 혼성층의 두께는 7초 적용군이 가장 얇고, 15초군과 30초군에서는 차이가 없었다. 4. Single bonding agent를 이용한 경우 두터운 $2-4{\mu}m$의 혼성층이 관찰된 반면, All-In-One bonding system(Prompt L-pop, 3M ESPE, USA)에서는 비교적 얇은 혼성층($1-2{\mu}m$)이 형성되었다.