초록
The steady-static creep behaviors of Ti-6Al-4V alloy, using the constant stress creep tester, were investigated over the temperature range of $510{\sim}550^{\circ}C$(0.42~0.44Tm) and the stress range of 200~275 MPa($20.41{\sim}28.06kg/mm^2$). The stress exponents(n) for the static creep deformation of this alloy were 9.85, 9.35, 9.24 and 8.85 at the temperature of 510, 525, 535 and $550^{\circ}C$, respectively. The stress exponent(n) decreased with increasing the temperature and became close to about 5. The apparent activation energies(Q) for the static creep deformation were 254.4, 241.8, 234.4 and 221.9 kJ/mole for the stress of 200, 225, 250 and 275MPa, respectively. The activation energy(Q) decreased with increasing the stress. From the above results, it can be concluded that the static creep deformation for Ti-6Al-4V alloy was controlled by the dislocation climb over the ranges of the experimental conditions. Larson-Miller Parameter(P) for the crept specimens of Ti-6Al-4V alloy under the static creep conditions was obtained as $P=(T+460)({\log}\;t_r+21)$. The failure plane observed by SEM showed up dimple phenomenon at all range.