Adsorption of Nitrogen Oxides on Manufactured Impregnated Activated Carbon Fibers with Potassium Hydroxide

In this paper, impregnated activated carbon fiber (IACF) was manufactured to pitch-based activated carbon fibers (ACF) with potassium hydroxide (KOH) by using wet impregnation method to raise nitrogen oxides ($NO_x$) adsorptivity. The properties of IACF were observed using EPMA, TGA and DSC and $NO_x$ adsorptivity was observed at high and low temperature. Before and after adsorption was analyzed using ToF-SIMS for examine surface characterization of adsorbed $NO_x$. The results showed that the better adsorptivity appeared for increasing KOH ratio. So, $NO_x$ adsorptivity showed result that is proportional between KOH and the adsorbed amount. On the other hand, adsorbent that manufactured without washing was better $NO_x$ adsorptivity than adsorbent that manufactured with washing. The behavior of adsorption show that crossing time of NO and $NO_2$ delayed for a rising adsorptivity. And NO ratio increased but $NO_2$ ratio decreased according as KOH ratio increases. $NO_x$ was confirmed through surface analysis that remain in $NO_2^-$ and $NO_3^-$ form on IACF surface.