Effect of Moulding Conditions on Properties of Table Top for Student Desk Manufactured by Wood Waste Materials

폐기 목질 재료로 제조한 학생용 책상 천판의 성능에 미치는 성형조건의 영향

This research was performed to investigate the effect of moulding conditions on properties of the table top for student desk manufactured by wood waste materials. The table top manufactured using the mat mixed properly with fine particles and coarse particles generally showed better physical properties than those manufactured using either fine particles or coarse particles did/ Especially, highest performance for overlaying was observed when fine particles were used for face layer and coarse particles were used for core layer. The internal bond (IB) strength, the bending strength and thickness swelling increased with the increase of density. Most of physical properties were improved with the increase of hot pressing temperature. The best physical properties were found at 190℃ when the first hot pressing and the second hot pressing times were two minutes. However, the effect of the second hot pressing time of two minutes on the physical properties was not markedly different from that of one minute. This result suggests that the second hot pressing time of one minute is enough to increase the productivity in manufacturing the table top with the least decrease of the physical properties.

폐기 목질재료를 사용하여 학생용 책상 천판의 성형시 각 제조조건에 따른 천판의 성능을 검토하였다. 책상 천판의 파티클 구성은 고운 파티클과 거친 파티클을 적절히 혼합한 것이 고운 파티클이나 거친 파티클만으로 제조한 것보다는 전체적으로 성능이 양호하였으며, 특히 표층에는 고운 파티클을 중충에는 거친 파티클을 구성하는 것이 표면 마감성이 가장 우수하였다. 그리고 밀도가 높을수록 박리강도, 휨 강도는 우수하나, 흡수두께 팽창율은 증가하였으며, 수지 도포량이 많을수록 박리강도, 흡수두께 팽창율은 양호하나, 포름알데히드의 방출량은 높았다. 가압온도는 높을수록 대부분의 성능이 향상되었으며, 190℃가 가장 적절하였다. 가압시간은 1단계 2분과 2단계 2분이 비교적 양호하나 2단계의 가압시간을 1분으로 단축하여도 성능에는 큰 문제가 없어 앞으로 생산성의 향상을 기대할 수 있을 것으로 생각된다.