Influence of Cure Accelerator Content on Change of Crosslink Density by Thermal Aging in Natural Rubber Vulcanizates Filled with Silica
실리카로 보강된 천연고무 가황물의 가교 밀도 변화에 가황촉진제 함량이 미치는 영향
-
Choi, Sung-Seen
(Advanced Materials Research Center, Chungnam National University) ;
- Nah, Changwoon (Department of Polymer Science and Technology, Chonbuk National University)
- Received : 2002.04.09
- Accepted : 2002.04.20
- Published : 2002.06.21
Abstract
The effect of cure accelerator content on the change in crosslink density by thermal aging was studied for silica-filled natural rubber (NR) vulcanizates. Influence of silane coupling agent was also investigated. N-tert-Butyl-2-benzothiazole sulfenamide (TBBS) and bis-(3-(triethoxysilyl)-propyl)-tetrasulfide (TESPT) were used as a cure accelerator and a silane coupling agent, respectively. The crosslink density increased by thermal aging and the increasing level became larger as the aging temperature increased. The degree of crosslink density change of the vulcanizates without the silane coupling agent was larger than that of the vulcanizates containing the silane coupling agent. For the vulcanizates silane coupling agent, the activation energy for the crosslink density change decreased with increase of the cure accelerator content in the vulvanizate.
실리카로 보강된 천연고무 가황물에서 가황촉진제의 양이 열노화에 의한 가교밀도의 변화에 미치는 영향에 대해 연구하였다. 또한 실란커플링제의 영향도 조사하였다. 가황촉진제로는 N-tert-butyl-2-benzothiazole sulfenamide(TBBS)를 실란 커플링제로는 bis-(3-(triethoxysilyl)-propyl)-tetrasulfide(TESPT)를 사용하였다. 가황물을 열노화 시키면 가교밀도는 증가하였고 노화 온도가 높을수록 그 변화 정도는 컸다. 실란 커플링제가 포함되지 않은 가황물의 가교밀도 변화가 실란 커플링제를 포함한 것에 비해 더 크게 나타났다. 실란 커플링제가 포함되지 않은 가황물의 경우에는 가교밀도의 변화에 대한 활성화 에너지가 가황촉진제의 함량이 증가할수록 순차적으로 낮아지는 경향을 보였다.
Keywords
- CROSSLINK DENSITY;
- THERMAL AGING;
- SILICA-FILLED NATURAL RUBBER VULCANIZATE;
- CURE ACCELERATOR;
- SILANE COUPLING AGENT