Oil Gelling Agents made from Polyurethane by One-Shot Method

One-Shot법을 이용한 폴리우레탄계 유겔화제의 특성

Polyurethane NCO prepolymers were synthesized with the polyols such as PTMG, GP and the isocyanate such as TDI at $40^{\circ}C$ for 8.5 minutes. As average molecular weights (${\bar{M_n}}$: 1000, 2000, 3000, 4000) of PTMG, and GP were decreased from 4000 to 1000, ratio of oil gelation increased from 298%, to 440%, for Bunker B. When oil and water were emulsified, the ratio of gelation was increased approximately two times. Ratio of gelation for emulsive Bunker B was increased from 402% to 910%, for PTMG1000 and increased from 440%, W 958% for GPI1000. Ratio of oil gelation for emulsive Bunk C which has higher viscosity than Bunker B was measured w 923% for PTMG1000 made with chain extender, i.e. EG, and measured to 1098% for GP1000. The gel made from GP which has three functional group showed soft and strong characteristic, as a result, it can be removed easily from oil spilled ocean.

물과의 발포반응에 의해 유츌유를 겔화할 수 있는 폴리우레탄 NCO prepolymer를 제조하기 위하여 폴리올(PTMG 및 GP)과 이소시아네이트(TDI)를 사용하여 NCO prepolymer를 합성하였다. 폴리올 각각의 분자량에 따라 합성한 NCO prepolymer를 이용하여 초기 유출유와 에멀젼된 유출유 그리고 유출유의 종류에 따라 유겔화율을 측정하였다. Bunker B 초기 유출유에 대하여 3관능성 폴리오인 GP1000의 경우 440%의 유겔화율은 나타내었으며, 유출유와 해수가 에멀젼(emulsion)된 상태에서는 2배 정도가 증가한 958%의 유겔화율을 나타내었다. 또한 Bunker B에 비해 점도가 높은 Bunker C의 에멀젼된 상태에서는 1098%의 유겔화율을 나타내었다. 사슬연장제가 투입된 2관능성 폴리올인 PTMG1000의 경우에는 에멀젼된 Bunker B에 대하여 910%의 유겔화율을 나타내었으며, 에멀젼된 Bunker C에 대하여 923%의 유겔화율을 나타내었다. 3관능성 폴리올을 사용하여 제조된 NCO prepolymer의 경우, 형성된 폴리우레탄 겔은 부드럽고 강한 특성을 가져 회수에 용이한 상태를 나타내었다.