Properties of Coating Film Containing Silicone acrylate
실리콘 아크릴레이트를 함유하고 있는 코팅필름의 물성
- Lee, Bong-Woo (Technical Research Center, Kunsul Chemical Industry Co.) ;
- Bang, Moon-Soo (Department of Advanced Materials Chemical Technology, Cheonam National Technical College) ;
-
Hong, Jin-Who
(Department of Polymer Science and Engineering, Chosun Univ.) ;
- Kim, Dae-Jun (Laboratory of Adhesion & Bio-Composites, School of Biological Resources and Materials Engineering, Seoul National University) ;
-
Kim, Hyun-Joong
(Laboratory of Adhesion & Bio-Composites, School of Biological Resources and Materials Engineering, Seoul National University)
- 이봉우 (건설화학기술연구소) ;
- 방문수 (천안공업대학 신소재 응용학과) ;
-
홍진후
(조선대학교 고분자공학과) ;
- 김대준 (서울대학교 생물자원공학부 바이오복합재료 및 접착과학연구실) ;
-
김현중
(서울대학교 생물자원공학부 바이오복합재료 및 접착과학연구실)
- Received : 2002.09.15
- Accepted : 2002.10.20
- Published : 2002.12.23
Abstract
Modern plastics are of great importance in many practical applications and their performance can be enhanced by surface modification to improve their hardness, wear and chemical resistance. The object of this study is invention of functional hardening coating materials which are applied to plastic, such as polycarbonate, polymethylmethacylate and acrylonitrilebutadienestyrene. In order to invention of hardening coating materials, we synthesized new silicone acrylate oligomer and prepared coating films containing silicone acrylate oligomer (SAOE) on PC substrate. The curing of coatings is performed by UV-radiation. As results of experiments, The properties of coating films which are contained SAOE is greatly improved in comparison with coating films non-contained SAOE. Especially, when 1 wt% SAOE was introduced into the coating formulation, the UV hardening coatings obtained showed the best surface hardness and gloss.
오늘날 플라스틱은 많은 분야에서 매우 중요한 역할을 하고 있으며, 플라스틱의 표면개질을 통해 경도, 마모, 내화학성과 같은 성질을 개선하여 성능을 향상시킬 수 있다. 본 연구의 목적은 polycarbonate, polymethylmethacrylate, acrylonitrilebutadienestyrene과 같은 플라스틱에 적용되는 기능성 하드코팅제를 개발하기 위한 것이다. 하드코팅제를 개발하기 위하여 먼저 실리콘아크릴레이트 올리고머(SAOE)를 합성하고, 이를 함유한 코팅필름을 PC 기재로 하였으며, 도막은 자외선경화에 의하였다. 실험의 결과에 의하면, SAOE를 함유하고 있는 도막의 물성이 SAOE를 함유하고 있지 않은 도막의 물성에 비해서 크게 향상되었다. 특히 코팅 조성물내에 1wt%의 SAOE가 함유되었을 때, 이로부터 얻어진 도막의 경도나 광택이 가장 우수함을 나타내었다.