Abstract
The stress-strain relationship of polymer concrete flexural member was evaluated using C-shaped polyester concrete specimen, the compressive strength of which is 1400 kgf/$\textrm{cm}^2$. Eccentric compression test was performed to estimate the parameters, ${\alpha}$, ${\beta}$1, ${\gamma}$ for equivalent rectangular stress block. The ultimate moment strength ware obtained from the bending test on reinforced polymer concrete beams which were prepared with S different tensile steel ratios with a shear span ratio of 4.0. These values were compared with theoretical ultimate moment strengths, which were obtained using the parameters ${\alpha}$=0.61 and ${\beta}$1=0.73 from stress-stain curves of C-shaped specimens. The results showed that, when tensile steel ratio was over 0.50 $\rho$b, the experimentally obtained moment strengths were well matched with theoretically calculated values. In order to develop accurate criteria for polymer concrete flexural members, however, many other expermental studies for parameter determination are necessary using C-shaped specimens which have various compressive strengths and different sizes.
본 연구에서는 압축강도 1400 kgf/$\textrm{cm}^2$ 를 갖는 불포화 폴리에스터 폴리머 콘크리트를 이용하여 제작한 C형 시험체에 대한 편심압축 시험을 통하여 폴리머 콘크리트 휨부재의 응력-변형률 관계를 구명하고 등가직사각형 응력블럭의 파라미터 $\alpha$, $\beta$1, ${\gamma}$를 산출하였다. 아울러 인장철근비를 달리하는 5종의 전단스팬비 4.0인 철근 보강 폴리머 콘크리트 보에 대한 휨시험에서 얻어진 극한모멘트 시험값과 C형 시험체 응력-변형률 곡선에서 산출되는 파라미터 $\alpha$=0.61, $\beta$1=0.73 를 이용하여 계산된 이론적인 극한모멘트 값을 비교하여 보았던 바, 인장철근비가 0.50 $\rho$b 이상일때 시험값과 이론값이 비교적 잘 부합됨을 확인 할 수 있었다. 그러나 폴리머 콘크리트 휨 부재에 대한 보다 정확한 설계기준의 마련을 위해서는 압축강도와 크기를 변수로 하는 C형 시험체에 대한 보다 많은 시험을 통한 파라미터의 체계적인 연구가 필요하다.