Generally polymer mortar and concrete using unsaturated polyester resin has high strengths and good chemical resistance. However it also has high brittleness and because of this reason, it is not used for the purpose that demands high resistance to impact. The purpose of this study is to improve the brittleness of unsaturated polyester mortar(UPE mortar) which could be used for the flooring material with recycled aggregates and UPE. Polyurethane liquid rubber(PU) and recycled aggregates were used to complement the brittleness and to recycle the resources respectively. The characteristics of mortar were investigated according to the molecular weight and substitution rate of PU. As the molecular weight and PU substitution rate were increased, the viscosity was increased, working life became fast and curing shrinkage was reduced. Compressive and flexural strengths were also reduced but tile brittleness was improved. Therefore, it is seemed that the improved WE mortar could be obtained by using polyurethane liquid rubber with the polyol of molecular weight 2000, 3000.
일반적으로 불포화 폴리에스테르 모르타르 및 콘크리트는 강도가 우수하고 내약품성이 좋지만, 취성적이어서, 내충격성이 요구되는 용도로는 사용하기 어렵다. 그러므로, 본 연구에서는 재생골재와 불포화 폴리에스테르 액상수지를 사용한 바닥마감재를 개발하기 위해 불포화 폴리에스테르 모르타르의 취성을 개선시켜보고자 하였다. 불포화 폴리에스테르 모르타르의 취성을 개선하기 위한 재료로 폴리우레탄 액상고무를 사용하였으며, 폴리올의 분자량과 폴리우레탄 액상고무의 치환율에 따른 모르타르의 특성을 검토했다. 실험결과, 폴리우레탄 액상고무의 사용에 따라 불포화 폴리에스테르 모르타르의 점도가 증가하였고, 경화수축은 감소하였다. 그리고, 모르타르내에 생성된 고무입자에 의해 압축강도 및 휨강도는 다소 저하하였지만, 내충격성이 향상되고, 휨파괴시험결과에서 파괴하중이후에도 급격한 파괴를 보이지 않는 결과를 얻을 수 있었다. 따라서, 본 연구의 결과는 폴리올의 분자량 2000, 3000인 폴리우레탄 액상고무를 불포화 폴리에스테르 모르타르에 사용하여 취성의 개선효과를 얻을 수 있다는 것을 제시하고 있다.