Preparation and Properties of PE Heterogeneous ion Exchange Membrane with Bead and Fibrous ion Exchanger

비드와 섬유이온교환체 고정 PE 불균질 이온교환막의 제조 및 특성

  • 황택성 (충남대학교 공과대학 화학공학과) ;
  • 박명규 (충남대학교 공과대학 화학공학과) ;
  • 강경석 (충남대학교 공과대학 화학공학과)
  • Published : 2002.09.01
Download PDF
⟨ Previous Next ⟩

Abstract

Heterogeneous ion exchange membranes were prepared by mixing polyethylene as matrix with bead and fibrous anionic ion exchangers at different mixing ratio. Generally, ion exchange capacities were increased with increasing the ratio of the fibrous ion exchanger content. The highest ion exchange capacity of the membrane was 1.86 meq/g at 30wt% IXF (ion exchange fiber) in the membrane. The water uptake, fixed ion concentration, and ion transport number of the membrane increased with increasing the content of the fibrous ion exchanger. However, the electrical resistivity of the membrane was decreased with increasing the content of the fibrous ion exchanger. The lowest electrical resistivity of 5$\Omega$/$\textrm{cm}^2$ was observed at 30 wt%of IXF.

본 연구는 폴리에틸렌 기재에 비드와 섬유상 이온교환체의 배합비를 달리하여 불균질 이온 교환막을 제조하였다. PE 불균질 이온교환막의 이온교환능은 섬유강 이온교환체의 양이 증가할수록 선형적으로 증가하였으며 30 wt%에서 최대 1.86 meq/g 이었다. 불균질 이온교환막의 함수율, 고정이온농도 및 이온운반율도 섬유상 이온교환체의 양이 증가할수록 증가하였나. 반면 불균질 이온교환막의 전기저항은 섬유상 이온교환체의 양이 증가할수록 감소하였으며, IXF (ion exchange fiber)의 혼합량이 30 wt%에서 5$\Omega$/$\textrm{cm}^2$으로 전기저항 값이 가장낮았다.

Keywords

References

  1. J.Atom.Energy Soc.Japan v.10 E.N. Ogata https://doi.org/10.3327/jaesj.10.672
  2. Industrial wastewater treatment technology(2nd Ed.) J.W. Patterson
  3. J.Polym.Sci. v.B2 K.A. Kun;R. Kunin
  4. J.Appl.Polym.Sci. v.17 W.L. Sederel;G.J. Dejong https://doi.org/10.1002/app.1973.070170920
  5. J.Polym.Sci. v.19 H. Halgen;G.J. Dejong;W.L. Sederal
  6. J.Polym.Sci. v.B3 K. Dusek
  7. J.Electrochem.Soc. v.142 S. Tsuneda;K. Saito;H. Mitsuhara;T. Sugo https://doi.org/10.1149/1.2043963
  8. Polym.Int. v.16 E.S.A. Hagazy;H.A.A. El-Rehim;N.A. Khalifa;S.M. Atwa;H.A. Shawky
  9. Synthetic Membranes Process v.11 G. Belfort
  10. Desalination v.86 Y. Oreu;Y. Egozy
  11. Ind.Eng.Chem.Process DES.DEV. v.25 T.C. Huang;R.S. Juang https://doi.org/10.1021/i200033a033
  12. J.Am.Chem.Soc. v.72 W. Juda;W.A. McRae https://doi.org/10.1021/ja01158a528
  13. J.Membrane Sci. v.2 K.J. Liu;F.P. Chlanda;K.J. Magasubramanian https://doi.org/10.1016/S0376-7388(00)83237-8
  14. J.Membrane Sci. v.8 E. Molau Gunther https://doi.org/10.1016/S0376-7388(00)82318-2
  15. Manufacture and Testing of Paper and Boards J.N. Stephenson
  16. Desalination v.59 George P. Simon https://doi.org/10.1016/0011-9164(86)90027-5
  17. Colloid and Polymer Sci. v.256 T. Sata;R. Izou https://doi.org/10.1007/BF01438033