Abstract
This experiment was carried out to examine the effects of La-Co substitution on Sr-ferrite. The magnetic properties of calcined and sintered materials varied with the substitutional amount of La and Co elements in Sr-ferrite. Anisotropy field and coercivity for Sr ferrite were increased with raising La-Co substitution amounts. The microstructure observation for Sr ferrite substituted by La-Co revealed that La-Co inhabited grain growth during calcination and promoted lateral grain growth during sintering. The relationship between $B_{r}$ and $_{i}$ /$H_{c}$ for La-Co substituted Sr-ferrite was found to be $B_{r}$$≒0.097_{i}$ /$H_{c}$/+4500. In case of $SrFe_{12}$ $O_{19}$, $B_{r} was 4090 G and $_{ i}$$H_{c}$ was 3560 Oe, but $B_{r}$ was 4080 G and and $_{i}$ $H_{c}$ was 4800 Oe for $Sr_{0.7}$ $La_{0.3}$ $Fe_{11.7}$ /$Co_{0.3}$ $O_{19}$.
스트론튬 페라이트에 포화자화를 높이기 위하여 Fe이온에 Co를 치환하고, 원소치환에 따른 전하보상차원으로 La를 동시 치환을 실시한 $_{l-x}$ La$Sr_{x}$ /$Fe_{12-x}$ $Co_{x}$ $O_{19}$ 조성에서 치환량 X=0에서 부터 X=0.5까지 0.1씩 변화하여 하소분말을 제조하여 하소분말 특성을 조사하고, 소결조제와 함께 미분쇄한 후 자장중 성형 및 소결하여 스트론튬 페라이트 자석을 제조하여 미세구조와 자기적 특성을 조사하였다. 스트론튬 페라이트에 La-Co 치환량이 증가할수록 하소 후 이방성자장과 하소분말의 보자력을 강하게 증가시키며, 하소후 결정크기가 작아지는 것으로 나타났다. 스트론튬 페라이트 자석은 La-Co의 치환량에 따라 회귀식 $B_{r}$ $≒0.097_{i}$ $H_{c}$ +4500의 함수적 관계를 나타내고 있으며, La-Co를 치환하지 않은 $SrFe_{12}$$O_{19}$ 조성에서 잔류자속밀도는 4090 G, 보자력은 3560 Oe를 나타내었으나, La-Co치환량 0.3인 $Sr_{0.7}$ $La_{0.3}$ $Fe_{11.7}$ $Co_{0.3}$ $O_{19}$ 조성에서 잔류자속밀도는 4080 G, 보자력은 4800 Oe 특성을 나타내었다.