Abstract
13%Cr martensitic stainless steel has been used mainly with a material for fish pre-processing machinery. However, it has not very nice cutting section because of little of the carbon content. Therefore, SUS420J2 steel that contents 0.3%C with high-strength in spite of the rust is used with a material for fish pre-processing machinery. However, studies on the corrosion characteristics of SUS420J2 steel are relatively rare. Especially, the corrosion phenomenon may cause serious degradation because the fish pre-processing machinery is exposed always to seawater environment. In this paper, the immersion corrosion test was carried out at seawater environment (pH=7.52) on SUS420J2 steel specimens that have various post-treatment conditions and its corrosion characteristics were evaluated. From test results, the specimens such as base metal, vacuum heat treatment, electrolytic polishing and tempering after quenching tend somewhat sensitive from the corrosion. In the case of vacuum heat treatment specimen of continuous immersion during 360 days, the weight loss ratio was high about seven times when compared with the different specimens. On the contrary, SUS420J2 steel specimen that has the heat treatment of tempering after quenching and the electrolytic polishing was less sensitive from the corrosion, and the weight loss ratio was very low.
SUS420J2강은 내식성이 우수하고 강도가 커서 어류가공용 기계의 재료로써 사용되어지고 있다. 그러나 이 역시 환경의 영향에 의하여 열화되고 있으며, 특히 후처리의 조건에 따라 그 정도가 심해질 수도 있다는 것을 알 수 있었다. 열처리 후 전해연마한 경우에 있어서는 부식의 정도가 미약하였으나 단일 후처리방법을 사용하였을 때에는 입계부식 및 공식의 영향이 커지고 부식생성물의 생성이 용이해졌다. 실험의 결과로부터 열처리후 전해연마한 SUS420J2강의 부식정도가 가장 덜 민감하게 나타났으므로, 어류 전처리 가공기계용 재료로서 SUS420J2강의 사용에 있어서는 열처리 후 전해연마의 방법으로 후처리를 하는 것이 바람직하다고 생각된다. 금후, 경도 및 표면상태의 파라미터(parameter)를 고려한 부식시험과 현장에서의 외력의 작용을 고려한 응력부식 실험이 결과도 병행되어져야만 한다고 생각한다