Change of Surface Temperature in Woodceramics Made from MDF(I) -Effect of Density and Burning Temperature-

MDF로 제조된 우드세라믹의 표면온도변화(I) -밀도 및 소성온도의 영향-

The following conclusions were obtained with measuring the surface temperature change of woodceramics which were made of MDF to identify usability of using them as a sub-material for heating system when installing Ondol heating floor. For this purpose, woodceramics were burned at the temperature of $650^{\circ}C$ and $800^{\circ}C$ 1. Surface temperature of woodceramics increased with the increase of density of woodceramics, but no significant difference was detected at the surface temperature when burning temperature was changed. 2. Surface temperature change under given temperature increased as time passed and it showed more increase in temperature at the burning temperature of 80$0^{\circ}C$. 3. Surface temperature change with the change in floor temperature increased u hen floor temperature increased and heating mechanism was fast with increase of measuring temperature.

본 연구는 MDF로 제조된 우드세라믹을 이용하여 온돌마루판 시공 시 하부소재로서의 사용가능성을 검토하고자 실시하였다. 650℃와 800℃로 소성하여 제조된 우드세라믹을 발열판 위에 올려놓고 발열판의 온도 및 시간의 경과에 따른 우드세라믹의 표면온도의 변화를 측정하였다. 우드세라믹의 표면온도는 밀도가 증가함에 따라 표면온도가 증가하였으며, 바닥온도의 변화에 따른 표면온도는 바닥온도가 증가함에 따라 표면온도가 증가하여, 측정온도가 높을수록 열전도가 빠름을 알 수 있었다. 그러나 우드세라믹 제조 시 소성온도에 따른 표면온도의 변화는 뚜렷한 차이를 발견할 수 없었다.