저탄소강재(SM25C)의 피로크랙 전파거동에 미치는 결정립 크기의 영향

The Influence of Grain Size on the Fatigue Crack Propagation Behavior in the Low Carbon Steel (SM26C)

  • 김건호 (군산대학교 해양생산학·기관공학부)
  • 발행 : 2002.01.01

초록

In this study, the rotary bending fatigue test was carried out with low carbon steel(SM25C). The specimens were heat-treated in order to change the grain size, and investigated items are fatigue limit, small crack initiation, fatigue crack propagation behavior and possibility of fatigue life prediction according to the different grain size. The summarized result are as follows ; Fatigue limit of the smooth specimen was dependent upon the grain size. The fatigue crack initiation of the small grain size specimen was delayed more than that of the large grain size specimen. And the small cracks of small grain size specimen were distributed in the narrow region of the main crack circumference contrary to the large grain size specimen. The main crack was grown along the grain boundary having co-alliance with small cracks. The experiment material has quantitatively disclosed the possibility of fatigue life prediction because the fatigue crack propagation behavior is dependent upon the grain size.

키워드

참고문헌

  1. fracture mechanics(2ed) fracture mechanics(2ed) T.L.Anderson
  2. 日本機械學會論文集 v.38 no.305 切欠き材疲のれに反ばす結晶粒大きさの影響 福原熙明
  3. 日本機械學會論文集 v.40 no.329 結晶粒の大きさお えた低炭素綱 平滑およ疲れ限度 中澤一(외 5인저)
  4. 日本機械學會論文集 v.43 no.370 低炭素鋼の高溫疲勞强度に及ぼす結晶粒寸法の影響 長谷川典彦(외 2인저)
  5. 大韓機械學會論文集 v.9 no.4 微小圓孔材의 疲勞크랙 擧動고 페라이트 結晶粒度 宋森弘;吳煥燮
  6. 日本機械學會論文集 v.36 no.281 結晶粒度のすべり發生, き裂發生, 進展におよぼす影響についで 吉川紀之(외 2인 저)
  7. 日本機械學會論文集(A) v.56 no.524 フェライト粒をそろえた3種の 炭素鋼の疲勞强度 西谷弘信(외 2인 저)
  8. 日本機械學會論文集 v.55 no.514 疲勞限度の結晶粒經依存性た及ばす豫ひずみの影響 長瀨康男(외 2인 저)
  9. 韓國舶用機關學會誌 v.19 no.2 미소원공을 갖는 선박 추진축재의 피로크랙전파거동에 관한 연구 鄭在康(외 1인 저)
  10. 日本機械學會論文集 v.42 no.354 小穴付き試驗片の回韓軸げ試驗によるき烈傳ば特性の評價 西谷弘信;森光武則