Abstract
We received 2 types flexible packaging films from two companies that laminated PET $16{\mu}m/dry$ lamination/aluminium foil $7{\mu}m/dry$ lamination/CPP $80{\mu}m$ films. For the reason of hot sealing's trouble through filling process, We separated each layer and compared thicks, film types and tested IR, DSC and sensory test. At the result, one sample's thick is different but film types is same between samples. Optimum hot-sealing conditions between two samples is $195^{\circ}C\;and\;210^{\circ}C$. The difference is $15^{\circ}C$. According to test of direct filling packaging process by four face fluid filling machine, two sample's sealing strength of hot-sealing is $4.76kg/cm2/15mm$(sample of optimum hot-sealing condition is $195^{\circ}C$) and $3.84kg/cm2/15mm(210^{\circ}C)$.
PET $16{\mu}m/dry$ lamination/Al-foil $7{\mu}m/dry$ lamination/CPP $80{\mu}m$의 사양으로 2개 업체에서 제조된 포장용 복합필름에서 제품 충전공정 중에서 발생한 열접착 트러블의 원인을 규명하고자 복합필름을 분리하여 각각의 두께와 재질이 제시된 사양과 일치하는지를 관능검사와 IR, DSC로 측정한 결과 1개 업체의 것이 차단층의 두께가 다르고 열접착층 필름의 재질은 비슷한 것임을 알았고, 시험기로 찾은 최적 열접착조건은 $195^{\circ}C$와 $210^{\circ}C$로 $15^{\circ}C$의 차이를 보였으며 이를 종형 4면 액체충전포장기로 직접 충전 포장하였을 때의 봉지의 열접착 강도를 비교한 결과 최적 열접착 조건 $195^{\circ}C$의 것은 평균 $4.76kg/cm^2/15mm,\;210^{\circ}C$의 것은 평균 $3.84kg/cm^2/15mm$이었다.