Immersion tests with artificial seawater were carried out to investigate the resistance to seawater attack of 5 types of cement matrices. From the results of compressive strength and length change, it was found that blended cement mortars due to mineral admixtures, were superior to portland cement mortars with respect to the resistance to seawater attack. Moreover, XRD analysis indicated that the peak intensity ratio of low heat portland cement(LHC) paste, in portland cement pastes, had better results, and so did that of blended cement Paste. Pore volume of pastes by mercury intrusion porosimetry method demonstrated that total pore volume of ordinary portland cement(OPC) paste had a remarkable increase comparing with that of other pastes. In case of immersion of artificial seawater, the use of ground granulated blast-furnace slag and fly ash, however, showed the beneficial effects of 56% and 32% in reduction of total pore volume, respectively.
국내에서 생산되는 5종류 시멘트로 제조한 시멘트 경화체의 해수침식에 대한 저항성을 알아보기 위한 목적으로 2배농도 인공 해수에 각각 400일 및 800일동안 침지시켜 모르타르의 압축강도 및 길이변화를 측정한 결과, 혼합시멘트계 모르타르가 광물질혼 화재의 영향으로 포틀랜드시멘트계 모르타르와 비교하여 좋은 결과를 나타내었다. 또한 시멘트 페이스트의 XRD분석에 의한 수 화 및 반응생성물의 피크강도비를 살펴보면, 포틀랜드시멘트계 페이스트 중 저열포틀랜드시멘트의 피크강도비가 가장 작았으며, 혼합시멘트계 페이스트의 경우 portlandite 및 brucite의 피크강도비가 포틀랜드시멘트계 페이스트보다 작았다. 인공해수 침식으 로 인한 시멘트 페이스트의 공극량을 수은압입법으로 측정한 결과에 의하면 보통포틀랜드시멘트 페이스트의 총공극량이 가장 크게 나타났으나, 포틀랜드시멘트에 고로슬래그미분말 및 플라이애시를 혼합한 혼합시멘트계 페이스트의 경우 총공극량이 각각 약 56% 및 약 32 % 정도 저감되는 효과가 있었다.