Abstract
These experiments were carried out to examine the effects of elemental substitution of Mn and La-Mn on Sr-ferrite. The calcined properties for the Mn and La-Mn substitution were examined, and the sintered magnetic properties were compared with the stoichiometric condition. The magnetic properties of calcined SrM and (La-Mn)$_{0.3}$-SrM composition were as follows, respectively; M$_{s}$ : 61.06 emu/g, $_{i}$H$_{c}$ : 4.45 kOe and M$_{s}$ : 61.06 emu/g, $_{i}$H$_{c}$ : 4.46 kOe. Also, the sintered ferrite magnets of Mn$_{0.3}$-SrM and [(La-Mn)$_{0.3}$-SrM exhibited a similar properties to the stoichiometric composition but the coercivity of (La-Mn)$_{x}$-SrM was decreased rapidly with x=0.5.
Sr 페라이트의 자기적특성을 향상시키기 위하여 화학량론적조성인 SrF $e_{12}$ $O_{19}$[SrM]에서 SrF $e_{12-x}$M $n_{x}$ $O_{19}$[M $n_{x}$-SrM] 및 S $r_{l-x}$L $a_{x}$F $e_{12-X}$M $n_{x}$ $O_{19}$[(La-Mn)$_{x}$-SrM] 조성으로 원료를 혼합한후 공기중 하소를 실시하여 하소분의 특성을 관찰하였으며, 소결조제와 함께 미분쇄 후 공기중에서 열처리하여 Sr 페라이트자석을 제조함으로써 그 자기적 특성변화를 조사하였다. 화학량론적 조성과 M $n_{0.3}$-SrM 조성으로 원소치환을 실시한 하소분말의 특성은 각각 $M_{s}$ : 61.06 emu/g, $_{i}$ $H_{c}$ : 4.45 kOe 및 $M_{s}$ : 61.06 emu/g, $_{i}$ $H_{c}$ : 4.46 kOe 로 거의 동일한 특성이 얻어졌다. 이것은 Sr페라이트의 화학량론적 조성에서 Mn원소를 대치한 경우, 결정구조의 변화없이 치환된 것으로 생각된다. 또한 화학량론적인 조성에서 M $n_{x}$-SrM 및 (La-Mn)$_{x}$-SrM 조성으로 원소치환된 하소분말을 사용하여 제조한 페라이트 자석의 자기특성은 소량첨가 (X=0.3)경우는 화학량론적인 조성과 거의 동일한 특성을 나타내나 치환량이 많아지면(X=0.5) 일반적으로 자기특성이 감소하였으며, 특히 $_{i}$ $H_{c}$ 값이 급격히 떨어짐으로써 (La-Mn)$_{x}$-SrM조성의 경우 x=0.3부근에서 최적의 치환량을 보여주었다.조성의 경우 x=0.3부근에서 최적의 치환량을 보여주었다.