Barium Hexaferrite Thin Films Prepared by the Sol-Gel Method

  • 발행 : 2001.03.01

초록

Nano-crystalline hexaferrite $BaFe_{12}O_{19}$(BaM) thin films have been prepared by the sol-gel method. A solution of Ba-nitrate and Fe-nitrates was dissolved in solvent with the stoichiometric ratio Ba/Fe=1/10. Films were spin-coated onto $SiO_2$Si substrates, dried and then heated in air at various temperatures. In films prepared at a drying temperature $T_d=250^{\circ}C$ and a crystallizing temperature 650${\circ}C$, single-phase BaM was obtained. High coercivities were obtained in these nano-crystalline thin films, 4~5.5 kOe for hexaferrite. Polycrystalline BaM/$SiO_2$/Si(100) thin films were characterized by Rutherford backscattering (RBS), thermogravimetry (TGA), differential thermal analysis (DTA), x-ray diffraction (XRD), and vibrating sample magnetometry (VSM), as well as Fourier transform infrared spectroscopy (FTIR). The perpendicular coercivity $H_{C\bot}$ and in-plane coercivity $H_{CII}$ after annealing at 650${\circ}C$ for 2 hours were 4766 Oe and 4480 Oe, respectively, at room temperature, under a maximum applied field of 10 kOe.

키워드

참고문헌

  1. J. Appl. Phys. v.87 no.9 C. S. Kim;S. Y. An;S. W. Lee
  2. J. Magn. Magn. Mater. v.177-181 no.241 Y. Hoshi;H. Shinozaki;H. Shimizu;K. Kato;F. Kaneko
  3. Appl. Phys. Lett. v.76 no.24 S. A. Oliver;S. D. Yoon;I. Kozulin;M. L. Chen;C. Vittoria
  4. J. Appl. Phys. v.71 no.6013 E. J. Donahue;D. M. Schleich
  5. Appl. Phys. Lett. v.63 no.2836 C. Surig;K. A. hempel;D. Bonnenberg
  6. J. Soild State Chem. v.126 no.161 P. Vaqueiro;M. P. Crosnier-Lopez;M. A. Lopez-Quintela
  7. IEEE Trans. on Magn. v.29 no.6 X. Y. Sui;M. H. Kryder;B. Y. Wong;D. E. Laughlin
  8. Aldrich Library of FT-IR Spectra Vol.Ⅰ,Ⅱ,Ⅲ Charles J. Pouchert
  9. J. Appl. Phys. v.79 no.9 A. Ishikawa;K. Tanahashi;M. Futamoto