Abstract
We investigated to DC magnetic characteristics, the dependence of annealing temperature on the crystal grain and the crystalline orientation for grain-oriented silicon ribbon with 100 $\mu\textrm{m}$ final thickness manufactured by three times cold rolling method using the hot-rolled silicon steel plate as a raw material. The growth of (110)[001] Goss texture were almost observed in the whole area of the sample. The values of the saturation magnetic flux density B$\sub$s/ and the average ${\alpha}$ angle have 1.9 T and 4.6 degrees respectively. From this result we could be confirmed that the three times cold rolling method has a possibility of manufacture for oriented ultra-thin silicon ribbons much more simple and cheeper than the existing oriented silicon steel manufacturing method by means of more simplified producing process.
열연판을 모재로 하여 압연 및 열처리 공정을 조합한 공정을 3회 냉간압연법을 사용하여 최종두께 100$\mu\textrm{m}$로 제작한 방향성 규소강대에 대하여, 직류자기 특성 및 결정입자의 열처리 의존성, 결정방위 등을 조사하였다. 그 결과, (110)면이 거의 시료 전체표면에 성장하는 것이 관측되었으며, B$_{8}$은 1.9 T정도, 평균$\alpha$각은 약 4.6$^{\circ}$이었다. 향후 약간의 (001)조직의 집적도 개선이 추가된다면, 염가의 열연판을 모재로 사용하여 기존의 방향성 규소강판의 경우보다 훨씬 제조공정수를 단순화함으로써, 경제성이 우수한 방향성 극박 규소강대를 제작할 수 있는 가능성을 확인하였다.