Abstract
An all solid-state thin film supercapacitor (TFSC) with Co$_3$O$_4$/LiPON/Co$_3$O$_4$ structure was fabricated on Pt/Ti/Si substrate using Co$_3$O$_4$ thin film electrode. Each Co$_3$O$_4$ film was grown by reactive dc reactive magnetron sputtering with increasing $O_2$/[Ar+O$_2$] ratio. Amorphous LiPON electrolyte film was deposited on Co$_3$O$_4$/Pt/Ti/Si in pure nitrogen ambient by using reactive rf magnetron sputtering. The electrochemical behavior of the Co$_3$O$_4$/LiPON/Co$_3$O$_4$ multi-layer structures exhibits a behavior of a bulk-type supercapacitor, even though much lower capacity (from 5 to 25 mF/$\textrm{cm}^2$-$\mu\textrm{m}$) than that of the bulk one. It was found that the TFSC showed a fairly constant discharge capacity with a constant current of 50 $\mu\textrm{A}/\textrm{cm}^2$ at the cut-off voltage 0-2V during 400 cycles. It is shown that the electrochemical behavior of the Co$_3$O$_4$/LiPON/Co$_3$O$_4$ TFSC is dependent upon the sputtering gas ratio. The capacity dependency of electrode films on different gas ratios was explained by different structural, electrical, and surfacical properties.
코발트 산화물 박막을 전극으로 하여 Pt/Ti/Si 기판위에 Co$_3$O$_4$/LiPON/Co$_3$O$_4$로 구성된 전고상의 박막형 슈퍼캐패시터를 제작하였다. 각각의 Co$_3$O$_4$박막은 반응성 dc 마그네트론 스퍼터를 이용하여 $O_2$/[Ar+O$_2$] 비를 증가 시키며 성장시켰고, 비정질 LiPON 고체전해질 박막은 순수한 질소분위기 하에서 rf 스퍼터링으로 성장시켰다. 비록 벌크 타입의 슈퍼캐패시터에 비해 낮은 전기용량 (5-25mF/$\textrm{cm}^2$-$\mu\textrm{m}$)을 가졌지만, Co$_3$O$_4$/LiPON/Co$_3$O$_4$ 구조로 제작된 전고상 박막형 슈퍼캐패시터는 벌크 타입과 비슷한 거동을 나타내었다 0-2V의 전압구간, 50$\mu\textrm{A}/\textrm{cm}^2$의 전류밀도에서 약 400사이클 까지 안정한 방전용량을 유지함을 관찰할 수 있었다 이러한 전고상 박막형 슈퍼캐패시터의 전기화학적 특성은 $O_2$/[Ar+O$_2$] 비에 의존하는데, 이러한 의존성을 구조적, 전기적 특성 및 표면특성을 분석하여 설명하였다.