Abstract
Intermetallics of Fe-28%Al($Fe_3Al$) and Fe-28%Al-4%Cr($Fe_3Al-4Cr$) were oxidized at 1073, 1273 and 1473k in air for up to 17 days. The oxidation resistance of$Fe_3Al-4Cr$ was basically similar to or better than that of $Fe_3Al$. The oxide scales formed on $Fe_3Al$ consisted essentially of pure ${\alpha}-AL_2O_3$, while those formed on $Fe_3Al-4Cr$ consisted of ${\alpha}-AL_2O_3$ having dissolved iron and chromium ions. The preferential outward diffusion of substrate elements to form the outer oxide layer led to the formation of Kirkendall voids at the oxide-matrix interface. The scales formed on $Fe_3Al(-4Cr)$ were thin and dense up to 1273K, but they spalled easily at 1473K, accompanied by more weight gains.
Fe-28%Al($Fe_3Al$)과 Fe-28%Al-4%Cr($Fe_3Al-4Cr$) 금속간화합물을 대기중 1073, 1273, 1473k의 온도에서 최고 17일까지 장시간 산화시켰다. $Fe_3Al-4Cr$의 산화저항은 근본적으로 $Fe_3Al$과 거의 비슷하거나, 약간 우수하였다. $Fe_3Al$ 위에 형성된 산화물은 거의 순수한 ${\alpha}-AL_2O_3$로만 구성되어 있었으며, $Fe_3Al-4Cr$ 위에 형성된 산화물은 약간의 Fe와 Cr 이온이 고용된 ${\alpha}-AL_2O_3$로 구성되어 있었다. 외부산화막을 형성하기 위해 모재원소의 외부확산에 의해 산화물-모재 계면에는 Kirkendall 기공이 존재하였다. $Fe_3Al(-4Cr)$ 표면에 형성된 산화막은 1273k가지는 비교적 얇고 치밀하였으나, 1473k에서 산화막의 박리와 함께 상대적으로 큰 무게증가가 발생하였다.