Life Prediction of Fatigue Crack Propagation and Nondestructive Evaluation in 5083 Aluminum Alloy

알루미늄 5083의 피로균열 진전에 따른 수명예측 및 비파괴평가

  • 남기우 (부경대학교 재료공학부)
  • Published : 2001.05.01
Download PDF
⟨ Previous Next ⟩

Abstract

fatigue life and nondestructive evaluation were examined experimentally using surface crack specimen and compact tension specimen of 5083 aluminium alloy. Acoustic emission signals emanated during failure of aluminum alloys has been the subject of numerous investigations. Possible sources of AE during deformation have been suggested as the dislocations, fracture of brittle particles and debonding of these particles from the alloy matrix. Fatigue life and penetration behavior of long surface crack can be evaluated quantitatively using K values proposed by authors. The influence of stress ratio on the frequency characteristics of AE signals were investigated.

Keywords

References

  1. 대한금속ㆍ재료학회지 v.38 no.11 고강도 구조용 내화강의 피로특성 및 음향방출 신호의 시간-주파수 해석 김현수;강창룡;남기우
  2. 대한기계학회논문집 v.5 no.6 고장력강의 피로수명과 균열관통거동에 관한 연구 남기우
  3. 한국해양공학회지 v.8 no.1 인장 굽힘피로를 받는 부재의 피로수명과 균열관통 남기우
  4. 한국해양공학회지 v.13 no.3 피로균열의 지연거동에 따른 수명예측 및 비파괴평가 남기우;김선진
  5. 한국해양공학회지 v.11 no.3 표면균열재의 피로균열관통거동에 따른 어코스틱에미션 남기우;김선진;이건찬;오정환;오세규;이주석
  6. 비파괴검사학회지 v.19 no.4 열화된 SUS316강의 시간-주파수 해석에 의한 비파괴평가 이건찬;오정환;남기우;이주석
  7. JSME Int. J. v.30 The Fatigue Life and Crack Through-Thickness Behaviour of a Surface-Cracked Plate (for the Case of Tensile Load) Ando, K.;Fujibayashi, S.;Nam, K. W.;Takahashi. M.;Ogura, N.
  8. Boiler and Pressure Vessel Code. Sec. XI ASME
  9. Engng. Fract. Mech. v.2 Fatigue Crack Closure under Cyclic Tension Elber
  10. IMCO resolution A 328(IX) Code for the Construction and Equipment of Ships Carring Liquefied Gases in Bulk
  11. Fatigue Fract. Engng. Mater. Struct. v.22 Acoustic Emission from Surface Fatigue Cracks in SS41 Steel Nam, K.
  12. Fatigue Fract. Engng. Mater. Struct. v.17 no.8 Fatigue Life and Penetration Behaviour of Surface-Cracked Plate under Combined Tension and Bending Nam, K. W.;Ando, K.;Ogura, N.;Matui, K.
  13. JSME Int.J. v.31 The Fatigue Life and Crack Through-Thickness Behaviour of a Surface-Cracked Plate (Effect of Stress Concentration) Nam, K .W.;Fujibayashi, S.;Ando, K.;Ogura, N.
  14. Fatigue Fract. Engng. Mater. Struct. v.16 The Effect of Specimen Size on the Behaviour of Penetration Fatigue Cracks Nam, K. W.;Ando, K.;Ogura, N
  15. Fatigue Fract. Engng. Mater. Struct. v.15 Leak-Before-Break Conditions of Plates and Pipes under High Fatigue Stresses Nam, K. W.;Ando, K.;Sakai, Y.;Ogura, N.
  16. Engng. Fract. Mech. v.15 An Empirical Stress Intensity Factor Equation for the Surface Crack Newman, J. C. Jr;Raju, I. S.
  17. Review of Progress in Quantitative Nondestructive Evaluation v.15 Joint Time-Frequency Processing of Ultrasonic Signals Malik, M. A.;Jin, X. M.;Sanile, J.