Abstract
Molybdenum thin films were deposited on the soda lime glass(SLG) substrates by direct-current planar magnetron sputtering, with a sputtering power density of $4.44W/cm^2$. The working pressure was varied from 0.5 mtorr to 20 mtorr to gain a better understanding of the effect of sputtering pressure on the morphology and microstructure of the Mo film. Thin films of $CU(InGa)Se_2$ (CIGS) were deposited on the Mo-coated glass by three stage co-evaporation process. The highest efficiency device was obtained at the maximum value of the tensive stress. The morphology of Mo-coated films were examined by using scanning electron microscopy The film's microstructure, such as the preferred orientation, the full width at half-maximum(FWHM), and the residual intrinsic stress were examined by X-ray diffraction.