초록
The mechanical and electrical properties of the hot-pressed and pressureless annealed SiC+39vol.%$TiB_2$electroconductive ceramic composites were investigated as a function of the liquid additives of $Al_2O_3+Y_2O_3$. The result of phase analysis for the SiC+39vol.%$TiB_2$composites by XRD revealed $\alpha$-SiC(6H), $TiB_2$, and $YAG(Al_5Y_3O_{12})4 crystal phase. The relative density of SiC+39vol.%$TiB_2$ composites was increased with increased $Al_2O_3+Y_2O_3$. contents. The fracture toughness showed the highest value of $7.8 MPa.m^{1/2}$ for composites added with 12 wt % $Al_2O_3+Y_2O_3$. additives at room temperature. The electrical resistivity and the resistance temperature coefficient showed the lowest value of $7.3\times10_{-4}\Omega.cm\; and\; 3.8\times10_{-3}/^{\circ}C$ for composite added with 12 wt% $Al_2O_3+Y_2O_3$. additives at room temperature. The electrical resistivity of the SiC+39vol.%$TiB_2$composites was all positive temperature coefficient resistance(PTCR) in the temperature ranges from $25^{\circ}C\; to\; 700^{\circ}C$.