Abstract
$YVO_{4}$ and Nd:$YVO_{4}$ single crystals have been grown developed Edge-defined film-fed growth (EFG) method and the crystals were measured on optical properties. $YVO_{4}$ and Nd:$YVO_{4}$ single crystal were transparent, high quality due to homogeneity of surface temperature of the melt and stability of meniscus during crystal growth. In transmittance and absorption spectra, Nd:$YVO_{4}$ single crystals had absorption peaks at wavelengths of 532, 593, 753, 808, 888 though $YVO_{4}$ single crystal had a broad transmittance at wavelength ranging from 340 to 1000nm. Also, Nd:$YVO_{4}$ single crystals had emissions of energy at range of 800~900 nm in photoluminescence (PL) spectrum.
Developed Edge-defined film-fed growth (EFG)법으로 $YVO_{4}$ 및 Nd:$YVO_{4}$ 단결정을 성장하였으며 성장된 결정의 광학적 특성을 측정하였다. $YVO_{4}$ 및 Nd:$YVO_{4}$ 단결정 모두 투명하였으며, 결정성장 동안 융액 표면 온도의 균질 및 meniscus의 안정화로 고품질의 결정을 얻을 수 있었다. 투과 및 흡수 스펙트럼 측정 결과에서 $YVO_{4}$ 단결정은 340 nm에서 1000 nm까지 대체로 넓은 영역에서 높은 투과율이 나타났지만, Nd:$YVO_{4}$ 단결정은 532, 593, 753, 807, 888 nm의 특정한 영역에서 흡수 peak들이 나타남을 획인할 수 있었다. 또한 Photoluminescence (PL) 스펙트럼을 측정한 결과, 800~900 nm의 영역에서 에너지 방출을 관찰할 수 있었다.