Abstract
EB-NMP free standing film is manufactured from NMP solution of polyaniline(emeraldine base EB). Also ES(emeraldine salt EB . HCl) film is manufactured by doping of EB-NMP film with 1 mole HCI aqueous solution. And EB-mixture films containing conductor(carbon black, graphite, Ag etc.) are prepared, In this study, electromagnetic interference shielding efficiency(EMI SE) of ES free standing film
($\sigma$=5 S/cm, t=0.14mm) is 23~25 dB in the frequency range of 10 MHz~1 GHz. ES-mixture(carbon black, graphite, Ag etc.) films, polyaniline film doped camphorsulfonic acid(CSA) show higher EMI SE(30~34 dB, 36~42 dB, 44~52 dB, 34~43 dB) property than that of ES free standing film, respectively.
Polyaniline(EB)/NMP 용액에 carbonblack, grahpite Ag를 첨가하여 우수한 막질의 free standing film을 제조하였다. 1 mole HCI로 도핑된 polyaniline(ES) free standing film($\sigma$=5 S/cm, t=0.14 mm)을 제조하여 10 MHz~1 GHz의 주파수 영역에서 전자기파 차폐효과를 측정한 결과 23~25 dB의 차폐효율을 나타내었으며, carbonblack, grahpite, AG을 첨가하여 제조한 ES free standing film 과 camphorsulfonic acid(CSA)를 도핑한 polyaniline film의 전자기파 차폐효율 측정결과 각각 30~34dB, 36~42dB, 44~52dB, 34~43dB로 ES free standing film 보다 우수한 특성을 나타내었다.