Scientific Analysis of the Neolithic Red Earthenwares(II)

신석기시대(新石器時代) 주칠토기(朱漆土器)의 과학적(科學的) 분석(分析)(II)

This study, a part of scientific analysis of the 23 Neolithic red earthenwares excavated from southeastern coast and islands. We analyzed earthenware through statistical method and hardness analysis of clay, following the analysis of clay composition, its firing temperature, pigment composition and its thickness. Clay composition was analyzed by using ICP-AES and XRF, and then Principal Component Analysis (one of multivariate methods) was used for classification. As a result, clay of the earthenware was classified into 3 groups(Bumbang, Youkjido and other sites). In addition, hardness analysis of pigment and clay based on the depth of earthenware surface showed that pigment layer containing lots of Fe₂O₃ had higher hardness than clay part, which can be interpreted that Fe₂O₃ contributes to raising hardness in case of high temperature firing. The fact that pigment hardness is higher than that of clay part implies that pigment was applied before firing.

본 연구는 동남해안 및 도서지방의 신석기시대 주칠토기 23점에 대한 과학적 분석의 일환으로서 먼저 태토성분, 소성온도, 안료성분 및 안료두께를 분석한 데에 이어 태토성분에 대한 통계적인 고찰 및 경도분석을 통한 안료성분의 역할을 보강하여 재정리한 것이다. 유도결합플라즈마분광기(ICP-AES)와 엑스선형광분석기(XRF)를 사용하여 태토의 성분분석을 실시하였고, 이 분석결과에 대한 다변량해석(PCA : 주성분분석법)을 수행한 결과, 토기의 태토는 범방, 욕지도, 나머지 지역의 3개 군으로 분류되었다. 또 태토와 안료의 경도를 토기 표면으로부터 깊이별로 측정한 결과, 산화철이 다량 포함된 안료층의 경도가 태토층보다 높았고 이를 통해 산화철이 고온소성시 경도를 크게 하는 역할을 했음을 알 수 있었다. 또한 안료층의 경도가 태토층 보다 높은 것은 안료층도 소성되었음을 의미하는 것으로, 토기성형시 안료를 먼저 바른 후 토기가 구워졌음을 유추해 볼 수 있다.