Experiment on Conservation Treatment Method(PEG, Sucrose and Lactitol) and Degree of State-change with RH of Waterlogged Archaeological Wood

수침고목재(水浸古木材)의 보존(保存)을 위한 PEG, Sucrose, Lactitol 처리(處理) 및 습도조건(濕度條件)에 따른 상태변화(狀態變化) 실험(實驗)

  • Yi, Yong-hee (Conservation Science Lab., The National Museum of Korea) ;
  • Kim, Soo-choul (Conservation Science Lab., The National Museum of Korea) ;
  • Park, Young-man (Conservation Science Lab., The National Museum of Kwangju) ;
  • Kim, Kyoung-su (Conservation Science Lab., The National Museum of Korea)
  • 이용희 (국립중앙박물관 보존과학실) ;
  • 김수철 (국립중앙박물관 보존과학실) ;
  • 박영만 (국립광주박물관 보존과학실) ;
  • 김경수 (국립중앙박물관 보존과학실)
  • Published : 2000.12.01
Download PDF
⟨ Previous Next ⟩

Abstract

In order to studies proper conservation treatment condition of waterlogged archaeological wood excavated from wetland in Shinchang-dong, Kwangju, 2 kinds of wooden objects were treated with PEG(Poly-Ethylene Glycol), sucrose and lactitol and their size stability and relative humidity were analyzed and compared each other. The result showed that Quercus spp. had the highest size stability in 2 Step-PEG treatment using PEG#200(MW:200) and PEG#4000 (MW:3,350) and Acer spp. was the highest in treatment using only PEG#4000. In relative humidity test after treatment 2 Step-PEG treatment showed the lowest size stability. In the meantime, sucrose and lactitol-treated sample was fast for penetration, sucrose-treated sample showed a sharp increase for penetration in as high as 84% humidity condition and medicine flew out a lot and lactitol-treated sample got enlarged with fine cracking(splitting) in relative humidity test. In relative humidity test, the samples showed cracking(splitting) in all treatment materials except for 2 Step-PEG treatment. This study showed that waterlogged archaeological wood excavated from Shinchang-dong had the highest size stability and highest adaptation to humidity change in case of treatment with 2 Step-PEG.

광주 신창동 저습지 유적에서 출토된 수침목재유물에 적합한 보존처리 방법을 설정하고자 동일유적에서 출토된 2종의 자연목재를 PEG(Poly-Ethylene Glycol), Sucrose, Lactitol로 처리하고 약제별 치수안정성 및 처리목재의 습윤↔건조 특성을 상호 비교하였다. 그 결과 상수리나무류는 저분자의 PEG#200(MW:200)과 고분자량의 PEG#4000(MW:3,350)을 이용한 2단계 PEG처리(PEG-2Step)에서, 단풍나무류는 PEG#4000만을 단독으로 적용한 처리에서 가장 높은 치수안정성을 나타내었다. 또한 처리 후 습윤↔건조 실험에서는 2단계 PEG처리한 시험재의 치수변화가 가장 작게 나타났다. 반면 Sucrose와 Lactitol의 경우 약제 확산속도가 빠르지만 Sucrose처리재는 84%의 높은 습도조건에서 흡습량이 급격히 증가하면서 약제가 다량 용출되었고, Lactitol은 습윤↔건조 후 미세한 할렬과 함께 처리재가 팽창되는 현상이 발생되었다. 또한 습윤↔건조 실험에서 2단계 PEG처리를 제외한 모든 시험재에서 갈라짐이 발생하였다. 이번 실험결과 신창동 저습지 출토수침목재는 2단계 PEG처리법을 적용한 경우에 치수안정성이 가장 높고 습도변화에 대한 적응성도 양호한 것으로 나타났다.