Determination of Metal Elements in Mongolian Chromite

몽골산 크롬철광 중의 금속성분 분석

The major and trace constituents of Mongolian chromite were analyzed by ICP-AES. The dissolution procedures, mixed acid ($HClO_4+H_3PO_4$) digestion and fusion with $Na_2O_2$ flux, have been studied to dissolve the chromite. The optimum dissolution method was found to be a fusion with $Na_2O_2$ flux. The effect of large amount of Na on major and trace constituents was examined when these elements were determined by ICP-AES. There was no effect on major elements at a concentration of Na 250 mg/L solution. The emission intensity of trace constituents containing Na 1,250 mg/L decreased to 1.0-5.2% according to elements and wavelengths. The result of this method was compared with that of neutron activation analysis (NAA) to confirm the accuracy of this procedure. The results between two methods were in a good agreement within less than 5% for $Al_2O_3$, $Cr_2O_3$, MgO and -20 to 8% for Co, Mn, V, Zn, respectively.

유도결합 플라스마 원자방출분광법(ICP-AES)을 이용하여 몽골산 크롬철광의 성분을 분석하였다. 크롬철광을 용해시키기 위하여 과염소산-인산의 흔합산과 융제로서 $Na_2O_2$의 적용성을 검토한 결과 최적의 용해방법은 용융법이었다. 크롬광의 주성분과 미량성분을 ICP-AES로 정량할 때 과량의 Na가 측정파장에 미치는 영향을 조사하였다. Al, Cr, Fe 및 Mg과 같은 주성분원소의 경우 Na가 250 mg/L까지 영향을 받지 않았으나, Co, Ni, Ti, V 및 Zn과 같은 미량성분들은 Na가 1,250 mg/L인 경우 측정원소와 파장에 따라 방출선의 세기는 1-5% 정도 감소하였다. 본 방법의 정확도를 확인하기 위하여 중성자방사화분석으로 얻은 결과와 상대편차를 비교하였다. $Al_2O_3$, $Cr_2O_3$, FeO 및 MgO의 경우에는 FeO를 제외하고 상대편차가 5% 이내이며, Co, Mn, V 및 Zn의 경우에는 ~20-8% 범위였다.