Abstract
The acrylonitrile copolymer/dimethylformamide (DMF) solutions were prepared to investigate the gelation behavior and critical gel concentration (c＊). Gelation is rapidly progressed with the increase of molecular weight of copolymer, but significantly delayed with supercooling temperature and comonomer contents. The c＊ behavior showed contrary trend against gelation behavior. In dynamic viscoelastic test, two glass-transition region were observed in film obtained from gelled solution whereas one glass-transition in film obtained from true solution. This result supports the idea that an ordered junction zone is formed by the dipole-dipole interaction of intermolecularly neighboring stereo-regular parts of atactic acrylonitrile copolymer chains due to a nucleation process in the solution.
분자량과 methylacrylate 함량이 다른 아크릴로니트릴 공중합체의 dimethylformamide (DMF) 농후용액의 겔화 거동 및 임계 겔농도 (c＊)를 조사하였다. 중합체 종류에 관계없이 저온에서 장시간 방치할 경우 방치시간에 따라 점도가 급격히 증가하여 겔화가 진행됨을 알았으며, 중합체의 분자량이 클수록, 방치온도가 낮을수록 그리고 공중합체 중 아크릴로니트릴 성분비가 증가할수록 겔화 진행속도가 증가하였고, 임계 겔농도는 감소하였다. 동적 점탄성 실험에서 겔 용액으로부터 얻은 필름은 진 용액으로부터 얻은 필름과 달리 두 개의 유리전이 영역을 나타내었다. 이러한 결과는 겔화과정에서 atactic 중합체중 입체 규칙적인 block들간의 쌍극자-쌍극자 상호작용에 의한 ordered junction zone의 존재를 강하게 시사하였다.