Evaluation of Piping Integrity in Thinned Main Feedwater Pipes

  • Published : 2000.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

Significant wall thinning due to flow accelerated corrosion(FAC）was recently reported in main feedwater pipes in 3 Korean pressurized water reactor(PWR) plants. The main feedwater pipes in one plant were repaired using overlay weld method at the outside of pipe, while those in 2 other plants were replaced with new pipes. In this study, the effect of the wall thinning in the main feedwater pipes on piping integrity was evaluated using finite element method. Especially, the effects of both the overlay weld repair and the stress concentration in notch-type thinned area on the piping integrity were investigated. The results are as follows : (1) The piping load carrying capacity may significantly decrease due to FAC. In special, the load carrying capacity of the main feedwater pipe was reduced by about 40% during about 140 months operation in Korean PWR plants. (2) By performing overlay weld repair at the outside of pipe, the piping load carrying capacity can increase and the stress concentration level in the thinned area can be reduced.

Keywords

References

  1. USNRC, 'Pipe Cracking Experience in LWR' , NUREG-0679 (1980)
  2. USNRC, 'Erosion/Corrosion-Induced Pipe Wall Thinning in US NPPs', NUREG-1344 (1989)
  3. USNRC, 'Investigation and Evaluation of Cracking Incidents in Piping in PWR' , NUREG-0691 (1980)
  4. American Society of Mechanical Engineer, ASME Boiler and Pressure Vessel Code Sec. XI, 'Rules for Inservice Inspection of Nuclear Power Plant Components'
  5. USNRC, Bulletin 87-01 'Thinning of Pipe Walls in Nuclear Power Plants' (1987)
  6. USNRC, Generic Letter 89-08, 'Erosion/ Corrosion-Induced Pipe Wall Thinning' (1989)
  7. American Society of Mechanical Engineer, ASME Boiler and Pressure Vessel Code Sec. III, 'Nuclear Components'
  8. American Society of Mechanical Engineer, ASME Code Case N-597, 'Requirements for Analytical Evaluation of Pipe Wall Thinning' (1998)
  9. American Society of Mechanical Engineer, ASME Code Case N-480, 'Examination Requirements for Pipe Wall Thinning due to Single Phase Erosion and Corrosion' (1990)
  10. American Society of Mechanical Engineer, ASME Code Case N-561, 'Alternative Requirements for Wall Thickness Restoration of Class 2 and High Energy Class 3 Carbon Steel Piping' (1996)
  11. American Society of Mechanical Engineer, ASME Code Case N-562, 'Alternative Requirements for Wall Thickness Restoration of Class 3 Moderate Energy Carbon Steel Piping' (1996)
  12. C. S. Hoemann and E. G. Berak, 'Engineering Evaluation of Erosion/Corrosion in Piping Systems', 10th SMIRT Conference, Vol. D, pp. 117-122 (1989)
  13. M. Ahammed, 'Prediction of Remaining Strength of Corroded Pressurized Pipelines', Int. Pressure Vessel & Piping, Vol. 71, pp. 213-217 (1997) https://doi.org/10.1016/S0308-0161(96)00081-6
  14. A. Deardorff, et al., 'Evaluation of Wall Thinning Due to Flow Accelerated Corrosion', ASME PVP Vol. 392, pp. 187-296 (1999)
  15. USNRC, Generic Letter 90-05 'Guidance for Performing Temporary Non-Code Repair of ASME Code Class 1, 2, and 3 Piping' (1990)
  16. ANSYS program, Swanson Analysis System Inc. (1987)
  17. G. Wilkowski and others, 'Degraded Piping Program - Phase II - Summary of Technical Results and Their Significance to Leak Before Break and In-Service Flaw Acceptance Criteria, March 1984-January 1989' , NUREG/CR-4082, Vol.8 (1989)
  18. C. Marschall and Others, 'Loading Rate Effects on Strength and Fracture Toughness of Pipe Steels Used in Task 1 of the IPIRG Program' , NUREG/CR-6098 (1993)
  19. A. Hopper and others, 'The Second International Piping Integrity Research Group (IPIRG-2) Program - Final Report' , NUREG/CR-6452 (1996)
  20. H. O. Fuchs and R. I. Stephens, 'Metal Fatigue in Engineering' . A Wiley Interscience