Characterization of Coating Layer formed on the Metal Surface by Calorizing

Calorizing(Aluminizing) 코팅 층의 표면특성 고찰

The effect of Particle size of coating Powder and coating temperature on the Properties of coating layer was studied by calorizing(or aluminizing). The surface properties of coating layer were fully characterized, using SEM and EDXS. Coating powders were separated according to the particle size by 3 steps and the coating temperature was varied from $950^{\circ}C$ to $980^{\circ}C$. Calorizing with pack cementation method carried under Ar atmosphere for 5 hrs. Results show that the thickness and Al content of coating layer increased as the size of coating powder decreased and coating temperature increased. And pores formed on the coating layer reduced and homogeneity of coating layer increased with smaller particle size of coating powder.

Calorizing(또는 Aluminizing)에서 코팅분말의 입자크기 및 코팅온도가 금속표면에 형성된 코팅 층의 특성에 미치는 영향을 SEM과 EDXS를 사용하여 자세히 고찰하였다. 코팅분말은 입자크기별로 3단계로 분리하여 사용하였으며 코팅온도는 950℃ 와 980℃로 변화하였다. Calorizing 처리는 팩 세멘테이션 방법을 사용하여 아르곤 분위기에서 5시간 동안 행하였다. Calorizing 처리 결과 코팅분말의 입자크기가 감소하고 코팅온도가 증가할수록 코팅 층의 두께와 코팅 층에서의 알루미늄의 함량이 증가하였다. 또한 오팅분말의 크기가 작은 경우(150-200 mesh) 코팅 층 표면에 형성된 기공이 현저히 감소하였고 표면의 균일성도 우수함을 알 수 있었다.