Abstract
The film-type specimen of poly ethylene terephthalate (PET) was stepwise elongated under tension with various speed range of about 0.5~500 mm/min, and then the necking behavior during its plastic deformation was observed. When elongated at the speed range of about 20~100 mm/min, stress oscillation was apparently occurred in the stress-strain curve. When elongated at the speed range of about 200~500 mm/min, stress oscillation was not did. The transparent/opaque zone and cross-section area in the specimen elongated at the speed of about 50 mm/min were examined using the optical microscopy and scanning electron microscopy. The corrosion characteristic of the specimen elongated at the speed of about 50 mm/min in 3.8 M NaOH alkali solution was examined using the optical microscopy.
필름형 poly ethylene terephthalate(PET)를 0~1000 mm/min의 속도로 단계적으로 연신시켰을 때, 플라스틱 변형이 일어나면서 형성되는 넥킹 거동을 조사하였다. 필름형 시편을 약 20~100 mm/min의 속도로 연신시켰을 때, 얻어진 응력-변형 곡선에서 응력 진동이 뚜렷하게 발생하였지만, 약 200~500 mm/min의 속도로 연신시켰을 때, 응력 진동이 발생하지 않았다. 약 50 mm/min의 속도로 연신된 시편에서 투명/불투명 존 및 단면을 광학 현미경과 주사형 전자 현미경으로 관찰하였다. NaOH 알칼리 용액 내에서 약 50 mm/min의 속도로 연신된 시편의 부식 특성을 광학 현미경으로 관찰하였다.