Stable amorphous calcium carbonate were synthesized from the serial work for the synthetic conditions such as concentration of solution, reaction temperature, aging time and pH of mother liquor. By using this as a precusor, calcite, aragonite and vaterite crystal particles were obtained in the water from adequate crystallization conditions. Furthermore, characterization for flourescence were performed by using crystals which were crystallized from the Sn dopped amorphous calcium carbonate. Calcite showed the most intensive emission and the center of emission wavelength was 464 nm with pure blue color. Calcite is expected to be used as phosphor for flourescent lamp because the maximum emission intensity was obtained from the excitation with 255 nm wavelength.
탄산칼슘을 모재로 한 형광체 제조를 위하여 비정질 탄산칼슘 전구체를 합성할 때 용액의 농도, 반응온도, 유지시간 및 모액의 pH의 영향을 조사함으로써 안정한 비정질 탄산칼슘을 합성할 수 있었으며, 물 속에 침적하여 결정화 조건을 달리하여 줌으로써 calcite, aragonite, vaterite의 결정 상을 얻을 수 있었다. 또한 활성원소로서 Sn을 첨가하여 비정질 탄산칼슘을 합성하고, 이를 결정화시켜 각 결정형에 따른 형광특성을 조사하였다. 결정형에 따른 발광강도는 calcite가 가장 우수하였으며, 발광중 심파장은 순수한 청색을 나타내는 464 nm였다. calcite의 발광강도는 여기파장 255 nm에서 최대가 되었으며, 형광램프용의 형광체로 사용하기 적합한 것으로 기대된다.