Strength Property Improvement of OCC-based Paper by Chemical and Mechanical Treatments (III) - Handsheet physical properties -

골판지 고지의 물리화학적 처리에 의한 강도향상(제3보) - 수초지의 물리적 특성변화 -

  • Lee, Jong-Hoon (Dept. of Forest Product, College of Agriculture, Chungnam National University) ;
  • Seo, Yung B. (Dept. of Forest Product, College of Agriculture, Chungnam National University) ;
  • Jeon, Yang (Dept. of Forest Product, College of Agriculture, Chungnam National University) ;
  • Lee, Hak-Lae (Dept. of Forest Product. College of Agriculture and Life Sciences, Seoul National University) ;
  • Shin, Jong-Ho (Pulp and Paper Research Center, KRICT)
  • 이종훈 (충남대학교 농과대학 임산공학과) ;
  • 서영범 (충남대학교 농과대학 임산공학과) ;
  • 전양 (충남대학교 농과대학 임산공학과) ;
  • 이학래 (서울대학교 농업생명과학대학 임산공학과) ;
  • 신종호 (한국화학연구소 펄프제지연구센터)
  • Published : 2000.06.01
Download PDF
⟨ Previous Next ⟩

Abstract

This study is a continuation of the previous experimental analysis and is mostly focused on handsheet strength properties. Four completely different fibers, which were Hw-BKP, SW-BKP, White ledger, and OCC, were selected to investigate the effect of mechanical pre-treatment by Hobart mixer on handsheet strehgth properties. After equal time mechanical pre-treatment, the fibers were refined with laboratory valley beater for 10, 20 and 30 minutes, and handsheets were prepared from the fibers for physical strength comparison. Handsheets from SW-BKP and OCC showed 5-30% increase of breaking length, burst index, tear index, and compression index while handsheets from HW-BKP and White ledger no increase except tear index. In Hobart mixer pre-treatment, HW-BKP and White ledger fibers were easily attached to the wall of the mixer bowl and mechanical action was not effectively applied. The fiber length of Hw-BKP and White ledger were 0.837 mm and 1.591 mm, respectively, while SW-BKP and OCC were 2.744 mm and 2.033 mm, respectively, in weight weighted length. The effective mechanical pre-treatment seems to be related to the fiber length. Tear indexes of the pre-treated furnish were much higher than no pre-treatment at the same breaking length level.

Keywords

References

  1. 펄프·종이기술 v.32 no.2 이종훈;서영범;전양;이학래;신종호
  2. Pulp technology and treatment for paper Clark, J.
  3. Properties of Paper: An Introduction Scott, W. E.
  4. TAPPI test methods TAPPI PRESS
  5. Mat. Res. Soc. Symp. Proc. v.197 Seth, R. S.
  6. The formation and structure of paper The interdependence of paper properties Gallay, W.;F. Bolam(ed.)
  7. Papermaking raw materials v.1 Page, D. H.;Seth, R. S.;Jordan, B. D.;Barbe, M. C.