Correlation of oxidation, Crosslinking, and Wear of UHMWPE

초고분자량 폴리에틸렌의 산화, 가교, 마멸과의 상관관계

  • 이권용 (대구대학교 자동차 ·산업 · 기계공학부) ;
  • 김석영 (영남대학교 금속 및 재료공학부) ;
  • 김신윤 (경북대학교 정형외과교실)
  • Published : 2000.08.01

Abstract

The effect of post-irradiation shelf-aging time on the wear of UHMWPE was investigated, and wear results were correlated with the time-dependent microstructural changes of polyethylene after gamma irradiation sterilization. The levels of oxidation and crosslinking in the shelf-aged acetabular liners were examined by FTIR and hot xylene extraction, respectively, and uni-directional repeat pass sliding wear tests were conducted by using a pin-on-disc wear tester. Gamma irradiation sterilization in the air environment caused an increase of oxidation, crosslinking, and wear resistance. With aging, however, oxidation progressed and decreased the level of crosslinking. This resulted in a decrease of wear resistance of UHMWPE that was accompanied with white bands and brittle cracking.

Keywords

References

  1. Clin. Orthop. v.311 The problem is osteolysis Harris, W. H.
  2. Biomaterials v.17 Gamma sterilization of UHMWPE articular implants: an analysis of the oxidation problem Premnath, V.;Harris, W. H.;Jasty, M.;Merrill, E. W.
  3. J. Biomed. Mater. Res. v.18 Property changes of UHMW polyethylene hip cup endoprostheses during implantation Eyerer, P.;Ke, Y. C.
  4. Clin. Orthop v.319 The Otto Aufranc Award, Impact of gamma sterilization on clinical performance of polyethylene in the hip Sutula, L. C.;Collier, J. P.;Saum, K. A.;Currier, B. H.;Currier, J. H.;Sanford, W. M.;Mayor, M. B.;Wooding, R. E.;Sperling, D. K.;William, I. R.;Kasprzak, D. J.;Surprenant, V. A.
  5. J. Biomed. Mater. Res. v.13 The effects of radiation sterilization on the properties of ultrahigh molecular weight polyethylene Nusbaum, H. J.;Rose, R. M.
  6. J. Appl. Polym. Sci. v.38 The effect of gamma radiation on the physical structure and mechanical properties of ultrahigh molecular weight polyethylene Birkinshaw, C.;Buggy, M.;Daly, S.
  7. Radiat. Phys. Chem. v.39 Improvement of polyethylene by irradiation in artificial joints Oonishi, H.;Takayama, Y.;Tsuji, E.
  8. J. KSTLE v.14 no.4 Effect of gamma-irradiation sterilization on the creep and wear of ultra-high molecular weight polyethylene Lee, K.-Y.;Lee, S. C.;Lee, K. H.
  9. Trans. SFB The fate of shelf-aged polyethylene acetabular liners Lee, K.-Y.;Pienkowski, D.;Jacob, R. J.;Hamilton, D. M.;Schroeder, D.;Higgins, J.
  10. Annual Bood of ASTM Standards v.08.02 Standard test methods for determination of gel content and swell ratio of cross-linked ethylene ASTM
  11. Trans. ORS Shelf-life effects on crosslinking of UHMWPE Patel, A.;Lee, K.-Y.;Hamilton, D. M.;Higgins, J.;Schroeder, D.;Pienkowski, D.
  12. Trans. SFB Improved resistance to oxidative degradation of 1900H net-shape compression molded components Gsell, R.;Lin, S.
  13. Trans. ORS Long term wear simulation of stabilized UHMWPE acetabular cups Essner, A.;Polineni, V. K.;Schmidig, G.;Wang, A.;Stark, C.;Dumbleton, J. H.
  14. Trans. ORS Marked improvement in the wear resistance of a new form of UHMWAPW in a physiologic hip simulator Jasty, M.;Bragdon, C. R.;O'Connor, D. O.;Muratoglu, O. K.;Premnath, V.;Merrill, E.;Harris, W. H.