Preparation of Aluminum Flake Powder by Recycling of Foil Scrap

알루미늄 호일 스크랩 재활용에 의한 플레이크 분말 제조

Recycling technology of aluminum foil scraps into aluminum flake powder by ball milling in dry or wet conditions was studied. Aluminum foil were laminated each other, elongated through microforging by the falling balls, fragmented into small foils and then changed into flake powder during ball milling. It is also possible to recycle foil scraps with thickness less than $60\mu\textrm{m}$ into aluminum paste by wet ball milling. As initial foil thickness decreases, foil is easily milled to flake powder by wet milling in mineral spirits. the appearance and the opaque character of glass painted with aluminum paste obtained by wet milling of foils are similar to those of aluminum paste made by ball milling of gas atomized powder.

알루미늄 호일 스크랩의 건식 및 습식 볼밀링에 의하여 알루미늄 플레이크 분말을 체조하는 재활용 기술에 대해 여 연구하였다. 볼밀링시 알루미늄 호일 스크랩들은 볼에 의한 미소 단조에 의하여 서로 층상으로 겹쳐지고 연산되면서 작은 호일로 쪼개진 후 플레이크 분말로 변하였다. 이러한 스크랩중에 $60\mu\textrm{m}$ 이하의 호일 스크랩은 볼밀링에 의하여 알루미늄 페이스트로 재활용이 가능하였고 초기 호일의 두께가 작을수록 쉽게 플레이크 분말화가 가능 하였다. 알루미늄 호일 스크랩의 봉밀링에 의하여 얻은 풀레이크 분말을 함유하는 알루미늄 페이스트와 가스 분사된 분말을 초기원료로 사용하여 불밀링한 플레이크 분말을 함유하는 페]이스트를 유리관위에 폐인팅한 후 외관 및 광택도를 비교한 결과, 그 특성은 유사하였다.